Overview of materials for Polyethersulfone, Carbon Fiber Reinforced

Category Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone, Carbon Fiber Reinforced
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyethersulfone, Carbon Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone, Carbon Fiber Reinforced". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.36 - 1.57 g/cc
0.0491 - 0.0567 lb/in³
Average value: 1.45 g/cc Grade Count:30
Filler Content 10.0 - 40.0 %
10.0 - 40.0 %
Average value: 19.6 % Grade Count:14
Water Absorption 0.100 - 1.50 %
0.100 - 1.50 %
Average value: 0.386 % Grade Count:15
Additive Loading 10.0 - 40.0 %
10.0 - 40.0 %
Average value: 23.3 % Grade Count:3
Linear Mold Shrinkage 0.000500 - 0.00400 cm/cm
0.000500 - 0.00400 in/in
Average value: 0.00188 cm/cm Grade Count:28
Melt Flow 12.1 - 15.3 g/10 min
12.1 - 15.3 g/10 min
Average value: 14.1 g/10 min Grade Count:3
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 90.0 - 325 MPa
13100 - 47100 psi
Average value: 146 MPa Grade Count:29
Elongation at Break 1.00 - 12.0 %
1.00 - 12.0 %
Average value: 2.35 % Grade Count:24
Elongation at Yield 1.30 - 2.80 %
1.30 - 2.80 %
Average value: 2.10 % Grade Count:5
Modulus of Elasticity 2.40 - 36.6 GPa
348 - 5300 ksi
Average value: 14.3 GPa Grade Count:30
Flexural Yield Strength 125 - 303 MPa
18100 - 44000 psi
Average value: 219 MPa Grade Count:28
Flexural Modulus 2.60 - 24.1 GPa
377 - 3500 ksi
Average value: 12.5 GPa Grade Count:29
Izod Impact, Notched 0.534 - 1.60 J/cm
1.00 - 3.00 ft-lb/in
Average value: 0.653 J/cm Grade Count:25
Izod Impact, Unnotched 3.74 - 6.94 J/cm
7.00 - 13.0 ft-lb/in
Average value: 5.15 J/cm Grade Count:24
Charpy Impact Unnotched 1.90 - 2.00 J/cm²
9.04 - 9.52 ft-lb/in²
Average value: 1.97 J/cm² Grade Count:3
Charpy Impact, Notched 0.450 - 0.600 J/cm²
2.14 - 2.86 ft-lb/in²
Average value: 0.550 J/cm² Grade Count:3
0.300 - 0.300 J/cm²

@Temperature -30.0 - -30.0 °C
1.43 - 1.43 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 0.300 J/cm² Grade Count:1
Thermal Properties Metric English Comments
CTE, linear 13.0 - 13.0 µm/m-°C

@Temperature 180 - 180 °C
7.22 - 7.22 µin/in-°F

@Temperature 356 - 356 °F
Average value: 27.9 µm/m-°C Grade Count:1
26.0 - 34.0 µm/m-°C

@Temperature 75.0 - 175 °C
14.4 - 18.9 µin/in-°F

@Temperature 167 - 347 °F
Average value: 27.9 µm/m-°C Grade Count:1
26.0 - 34.0 µm/m-°C

@Thickness 2.00 - 4.00 mm
14.4 - 18.9 µin/in-°F

@Thickness 0.0787 - 0.157 in
Average value: 27.9 µm/m-°C Grade Count:1
CTE, linear, Transverse to Flow 19.5 - 25.0 µm/m-°C

@Temperature 75.0 - 175 °C
10.8 - 13.9 µin/in-°F

@Temperature 167 - 347 °F
Average value: 22.3 µm/m-°C Grade Count:1
19.5 - 25.0 µm/m-°C

@Thickness 2.00 - 4.00 mm
10.8 - 13.9 µin/in-°F

@Thickness 0.0787 - 0.157 in
Average value: 22.3 µm/m-°C Grade Count:1
Maximum Service Temperature, Air 180 - 200 °C
356 - 392 °F
Average value: 190 °C Grade Count:4
Deflection Temperature at 0.46 MPa (66 psi) 207 - 210 °C
405 - 410 °F
Average value: 208 °C Grade Count:4
Deflection Temperature at 1.8 MPa (264 psi) 146 - 410 °C
295 - 770 °F
Average value: 216 °C Grade Count:27
Flammability, UL94 V-0
V-0
Grade Count:21
Electrical Properties Metric English Comments
Electrical Resistivity 100 - 9.90e+9 ohm-cm
100 - 9.90e+9 ohm-cm
Average value: 6.61e+8 ohm-cm Grade Count:19
Surface Resistance 4000 - 1.00e+12 ohm
4000 - 1.00e+12 ohm
Average value: 1.17e+11 ohm Grade Count:9
Insulation Resistance 100000 - 1.00e+6 ohm
100000 - 1.00e+6 ohm
Average value: 775000 ohm Grade Count:4
Static Decay 2.00 sec
2.00 sec
Average value: 2.00 sec Grade Count:5
Processing Properties Metric English Comments
Processing Temperature 80.0 - 366 °C
176 - 690 °F
Average value: 322 °C Grade Count:9
Nozzle Temperature 340 - 360 °C
644 - 680 °F
Average value: 350 °C Grade Count:4
Melt Temperature 343 - 390 °C
650 - 734 °F
Average value: 362 °C Grade Count:24
Mold Temperature 120 - 200 °C
248 - 392 °F
Average value: 157 °C Grade Count:28
Drying Temperature 140 - 150 °C
284 - 302 °F
Average value: 149 °C Grade Count:24
Moisture Content 0.0400 %
0.0400 %
Average value: 0.0400 % Grade Count:19
Dew Point -31.7 °C
-25.0 °F
Average value: -31.7 °C Grade Count:19
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi
Average value: 86.2 MPa Grade Count:23