COI Ceramics Sylramic™ S300 Silicon Carbide Ceramic Matrix Composite, SiC

Category	Ceramic , Carbide , Ceramic Matrix Composite
Manufacturer	COI Ceramics
Trade Name	Sylramic™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	COI Ceramics Sylramic™ S300 Silicon Carbide Ceramic Matrix Composite, SiC.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Engineered ceramic composite structures for a broad range of industries and applications.Reinforcing Fiber Flexibility: S300 - Sylramic SiC Preceramic Polymer Matrix Precursors: S300 - Crystalline (SiC + Si3N4) or SiCPhysical Attributes: Dense Matrix (

Mechanical Properties	Metric	English	Comments
Tensile Stress	75.8 MPa @Strain 0.0500 %	11000 psi @Strain 0.0500 %	Process Temperature T4
	75.8 MPa @Strain 0.0500 %	11000 psi @Strain 0.0500 %	Process Temperature T1
	82.7 MPa @Strain 0.0500 %	12000 psi @Strain 0.0500 %	Process Temperature T2
	89.6 MPa @Strain 0.0500 %	13000 psi @Strain 0.0500 %	Process Temperature T3
	138 MPa @Strain 0.100 %	20000 psi @Strain 0.100 %	Process Temperature T4
	145 MPa @Strain 0.100 %	21000 psi @Strain 0.100 %	Process Temperature T1
	148 MPa @Strain 0.100 %	21500 psi @Strain 0.100 %	Process Temperature T2
	159 MPa @Strain 0.100 %	23000 psi @Strain 0.100 %	Process Temperature T3
	183 MPa @Strain 0.150 %	26500 psi @Strain 0.150 %	Process Temperature T4
	193 MPa @Strain 0.150 %	28000 psi @Strain 0.150 %	Process Temperature T1
	200 MPa @Strain 0.150 %	29000 psi @Strain 0.150 %	Process Temperature T2
	214 MPa @Strain 0.150 %	31000 psi @Strain 0.150 %	Process Temperature T3
	228 MPa @Strain 0.200 %	33000 psi @Strain 0.200 %	Process Temperature T4
	241 MPa @Strain 0.200 %	35000 psi @Strain 0.200 %	Process Temperature T1
	248 MPa @Strain 0.200 %	36000 psi @Strain 0.200 %	Process Temperature T2
	262 MPa @Strain 0.200 %	38000 psi @Strain 0.200 %	Process Temperature T3