PolyOne Stat-Tech™ AT-10CF/000 Acetal (POM) Copolymer

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer	PolyOne Corporation
Trade Name	Stat-Tech™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Stat-Tech™ AT-10CF/000 Acetal (POM) Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Stat-Tech™ Electrically Conductive Compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic equipment applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber, for low to high levels of conductivity depending upon application requirements.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.43 g/cc	1.43 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm	0.0040 - 0.0060 in/in	ASTM D955
Linear Mold Shrinkage, Transverse	0.022 - 0.026 cm/cm	0.022 - 0.026 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	62.3 MPa	9040 psi	ASTM D638
Elongation at Break	2.3 %	2.3 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	11.7 GPa	1700 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	107 MPa	15500 psi	ASTM D790
Flexural Modulus	7.38 GPa	1070 ksi	ASTM D790
Izod Impact, Notched	0.370 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	0.693 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	161 °C @Thickness 6.35 mm	322 °F @Thickness 0.250 in	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	141 °C @Thickness 6.35 mm	286 °F @Thickness 0.250 in	Unannealed; ASTM D648

Electrical Properties	Metric	English	Comments
Volume Resistivity	100 - 10000 ohm-cm	100 - 10000 ohm-cm	ASTM D257
Surface Resistance	100 - 10000 ohm	100 - 10000 ohm	ASTM D257
Static Decay	0.0030 sec	0.0030 sec	(Mil-B-81705C), 12% RH, 5000 kV to 50 kV

Processing Properties	Metric	English	Comments
Melt Temperature	199 - 210 °C	390 - 410 °F

Descriptive Properties	Value	Comments
Features	Antistatic
	Conductive
	Electrically Conductive
	Statically Conductive
Filler / Reinforcement	Carbon Fiber Reinforcement, 10% Filler by Weight
Forms	Pellets
Generic Material	Acetal (POM) Copolymer
Generic Name	Acetal (POM) Copolymer
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant
Uses	Aerospace Applications
	Automotive Electronics
	Business Equipment
	Computer Components
	Connectors
	Electrical Housing
	Electrical/Electronic Applications
	Housings