SABIC Innovative Plastics Lexan® 4501 PPC (Asia Pacific)

Category Polymer , Thermoplastic , Polyphthalate Carbonate
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® 4501 PPC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High heat resistant polyphthlate carbonate, provides DTUL of 290F at 264 psi.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.19 g/cc
0.0430 lb/in³
ASTM D792
Water Absorption 0.16 %

@Time 86400 sec
 0.16 %

@Time 24.0 hour
 ASTM D570
Linear Mold Shrinkage, Flow 0.0070 - 0.0080 cm/cm

@Thickness 3.20 mm
 0.0070 - 0.0080 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 3.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 3.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 85
85
ASTM D785
Hardness, Rockwell R 122
122
ASTM D785
Tensile Strength at Break 71.0 MPa
10300 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 65.0 MPa
9430 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 122 %
122 %
Type I, 50 mm/min; ASTM D638
Flexural Yield Strength 95.0 MPa
13800 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.02 GPa
293 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 6.40 J/cm
12.0 ft-lb/in
ASTM D256
Izod Impact, Unnotched 32.04 J/cm
60.02 ft-lb/in
ASTM D4812
Tensile Impact Strength 577 kJ/m²
275 ft-lb/in²
Type S; ASTM D1822
Dart Drop, Total Energy 149 J
110 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 91.8 µm/m-°C

@Temperature -40.0 - 95.0 °C
 51.0 µin/in-°F

@Temperature -40.0 - 203 °F
 ASTM E 831
Specific Heat Capacity 1.25 J/g-°C
0.299 BTU/lb-°F
ASTM C351
Thermal Conductivity 0.210 W/m-K
1.46 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 1.8 MPa (264 psi) 143 °C

@Thickness 3.20 mm
 289 °F

@Thickness 0.126 in
 unannealed; ASTM D648
UL RTI, Electrical 125 °C
257 °F
UL 746B
UL RTI, Mechanical with Impact 125 °C
257 °F
UL 746B
UL RTI, Mechanical without Impact 125 °C
257 °F
UL 746B
Flammability, UL94 V-2

@Thickness 1.47 mm
 V-2

@Thickness 0.0579 in
 UL 94
Optical Properties Metric English Comments
Refractive Index 1.60
1.60
ASTM D542
Haze 1.0 %

@Thickness 2.54 mm
 1.0 %

@Thickness 0.100 in
 ASTM D1003
Transmission, Visible 85 %
85 %
2.54 mm; ASTM D1003
Electrical Properties Metric English Comments
Volume Resistivity >= 2.60e+16 ohm-cm
>= 2.60e+16 ohm-cm
ASTM D257
Dielectric Constant 3.0

@Frequency 1.00e+6 Hz
 3.0

@Frequency 1.00e+6 Hz
 ASTM D150
3.15

@Frequency 50.0 - 60.0 Hz
 3.15

@Frequency 50.0 - 60.0 Hz
 ASTM D150
Dielectric Strength 20.2 kV/mm

@Thickness 3.20 mm
 513 kV/in

@Thickness 0.126 in
 in air; ASTM D149
Dissipation Factor 0.0012

@Frequency 50.0 - 60.0 Hz
 0.0012

@Frequency 50.0 - 60.0 Hz
 ASTM D150
0.024

@Frequency 100 Hz
 0.024

@Frequency 100 Hz
 ASTM D150
Comparative Tracking Index 175 - 250 V
175 - 250 V
UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI 0.00 - 15 arcs
0.00 - 15 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746A
Descriptive Properties Value Comments
Specific Volume 0.83cm^3/g
ASTM D792