SABIC Innovative Plastics LNP THERMOCOMP RX10408H PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RX10408H PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* RX10408H is a compound based on Nylon 66 containing Proprietary Fillers. Characteristics are: Radiopacity and Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 |
| Density | 1.53 g/cc | 0.0553 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.640 % | 0.640 % | 50% RH, 24 hrs; ASTM D570 |
| 0.990 % | 0.990 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 191 MPa | 27700 psi | 5 mm/min; ISO 527 |
| 196 MPa | 28400 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 197 MPa | 28600 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.9 % | 2.9 % | Type I, 5 mm/min; ASTM D638 |
| 2.9 % | 2.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 12.42 GPa | 1801 ksi | 1 mm/min; ISO 527 |
| 12.58 GPa | 1825 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 277 MPa | 40200 psi | ISO 178 |
| 294 MPa | 42600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 10.17 GPa | 1475 ksi | 2 mm/min; ISO 178 |
| 11.0 GPa | 1600 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.9 J/cm | 22.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 73.0 kJ/m² | 34.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 61.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
33.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 256 °C | 493 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 251 °C | 484 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 254 °C @Thickness 3.20 mm |
489 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PP CCP20020 UV Polypropylene, Mineral Reinforced, UV stabilized
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Plastolein 9057 Plasticizer
- Materion BrushCAST® 275C High Strength Casting Alloy (Solution Annealed & Aged)
- Shakespeare ISOray Fluoropolymer UV resistant sewing thread, diameter 0.012"
- Solvay Specialty Polymers Tecnoflon® BR 9151 Fluoroelastomer
- Struktol STRUKSILON 8030 Silicone Stabilizer for PU-Rigid Foam
- A. Schulman SCHULAMID® 66 GF15H 15% Glass Fiber Reinforced, Heat Stabilized Nylon 66
- BASF Ultraform® S2320 0035 LEV POM
- 3M Scotchcal™ ElectroCut™ 7125-47 Graphic Film
- ArcelorMittal TRIP 780 Very high strength steel, Cold Rolled Steel
Copyright © lookpolymers.com All Rights Reserved