- Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 254 °C
Polymer Property : Deflection Temperature at 1.8 MPa (264 psi) = 254 °C Product List
Thermal PropertiesTips: 30 items are displayed at most.
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) |
254
°C @Thickness 3.18 mm |
489
°F @Thickness 0.125 in |
Unannealed; ASTM D648 |
|
PolyOne Edgetek® NN-20CF/000 BLACK Polyamide 66 (Nylon 66)
The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
254
°C @Thickness 3.18 mm |
489
°F @Thickness 0.125 in |
Annealed; ASTM D648 |
|
PolyOne Edgetek® NN-50GF/000EM L Polyamide 66 (Nylon 66)
Information provided by PolyOne
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 - 380 °C | 489 - 716 °F | Average value: 322 °C Grade Count:5 |
|
Overview of materials for Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polyetherketoneetherketoneketone (PEKEKK), Glass Fiber Filled". Each property range of values reported i..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | ASTM D-648 |
|
PlastiComp Complet® LCF20/LGF20 – PA66 BLK Polyamide 66, 40% Long Carbon/Glass Fiber
Composite PelletsInformation provided by PlastiComp, Inc.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | Annealed; ASTM D648 |
|
Solvay Specialty Polymers Amodel® AT-1116 HS Polyphthalamide (PPA)
(Unverified Data**)
Amodel AT-1116 HS polyphthalamide (PPA) is a toughened, heat stabilized 16% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stabi..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | ISO 75/Af |
|
Solvay TECHNYL® A 218 V30 Black 21 NHFE PA66, 30% glass fiber, DRY
Description: TECHNYL® A 218 V30 BLACK 21NHFE is a polyamide 6.6, high flow, reinforced with 30% of glass fiber, heat stabilized, for injection molding. This product is available in black color.Be..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
254
°C @Thickness 3.20 mm |
489
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Lubricomp RFL16S PA 66
LNP* Lubricomp* RFL16S is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Heat Stabilized.This data was supplied by ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
254
°C @Thickness 3.20 mm |
489
°F @Thickness 0.126 in |
unannealed; ASTM D 648 |
|
SABIC Innovative Plastics LNP Lubricomp RFL16S PA 66 (Asia Pacific)
LNP* Lubricomp* RFL16S is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Heat Stabilized.This data was supplied by ..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | ASTM D648 |
|
Techmer ES Electrafil® J-1/CF/30/TF/15 Nylon 66, 30% Carbon Fiber Reinforced, PTFE Lubed
Carbon Fiber Reinforced, PTFE Lubricated
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6/6 GF25 L BK 25% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 25% Filler by WeightAdditive: Heat Stabilizer and LubricantFeatures: Lubricated and Heat StabilizedAppearanc..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6/6 GF35 HS L 35% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 35% Filler by WeightAdditive: Lubricant and Heat StabilizerFeatures: Lubricated and heat StabilizedProcessin..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
|
Techmer ES HiFill® PA6/6 GF35 L UV 35% Glass Filled (Dry)
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 35% Filler by WeightAdditive: Lubricant, UV Stabilizer and Heat StabilizerFeatures: Lubricated, Good UV Resi..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
|
Techmer ES Luriblend® PA6/6 GF30 TL15 BK 30% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: Heat Stabilizer and PTFE Lubricant(15%)Features: Lubricated, Good Wear Resistance, Low Frict..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
|
Techmer ES Luriblend® PA6/6 GF33 TL15 BK 33% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 33% Filler by WeightAdditive: Heat Stabilizer and PTFE Lubricant(15%)Features: Lubricated, Good Wear Resistance, Heat Stab..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
|
Techmer ES Luriblend® PA6/6 GF33 TS15 BK 33% Glass Filled
Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 33% Filler by WeightAdditive: Heat Stabilizer, Silicone Lubricant and PTFE Lubricant(15%)Features: Lubricated, Good Wear R..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | ASTM D648 |
|
Techmer ES Plaslube® J-1/30/TF/22 BK223 PA66 |
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
254
°C @Thickness 3.20 mm |
489
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP RF009H PA 66
LNP* THERMOCOMP* RF009H is a compound based on Nylon 66 resin containing 45% Glass Fiber. Added feature of this material is: Healthcare.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP RF00BS PA 66 (Asia Pacific)
LNP* Thermocomp* RF00BS is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP RF00C PA 66 (Europe-Africa-Middle East)
LNP* Thermocomp* RF00C is a compound based on Nylon 66 resin containing Glass Fiber.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP Thermocomp RF00CS PA 66
LNP* Thermocomp* RF00CS is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.This data was supplied by SABIC-IP for the Americas re..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP RF00CSXS PA 66 (Asia Pacific)
LNP* Thermocomp* RF00CSXS is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) |
254
°C @Thickness 3.20 mm |
489
°F @Thickness 0.126 in |
unannealed; ASTM D648 |
|
SABIC Innovative Plastics LNP THERMOCOMP RX10408H PA 66
LNP* Thermocomp* RX10408H is a compound based on Nylon 66 containing Proprietary Fillers. Characteristics are: Radiopacity and Healthcare.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | ISO 75/Af |
|
Solvay TECHNYL® A 218W V30 Natural PA66, 30% glass fiber, DRY
Description: TECHNYL® A 218W V30 Nat is a polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection molding. This product is available in natural color.Benefits: The produc..
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
|
SABIC Innovative Plastics LNP THERMOCOMP RC00A PA6.6 (Europe-Africa-Middle East)
LNP* THERMOCOMP* RC00A is a compound based on PA6.6 resin containing Carbon Fiber. Added features include: Electrically Conductive
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | ASTM D648 |
|
A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | ASTM D648 |
|
A. Schulman SCHULAMID® 66 GF20H 20% Glass Fiber Reinforced, Heat Stabilized Nylon 66
Information provided by A. Schulman.
|
|||
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | ASTM D648 |
|
Clariant Renol PA113G33 Nylon 66, 33% Glass Fiber, Heat Stabilized, Lubricated
Data provided by Clariant Masterbatches
|
|||