Industrial Laminates/Norplex NP630 Paper Base Laminate

Category Polymer , Thermoset
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP630 Paper Base Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Machining grade with good electrical properties and moisture resistance. Low cold flow with good dimensional stability. Thickness Tested: 0.062", 0.125", and 0.500"
Physical Properties Metric English Comments
Specific Gravity 1.35 - 1.45 g/cc

@Thickness 1.57 mm
 1.35 - 1.45 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 1.3 %

@Thickness 1.57 mm
 1.3 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 90 - 110

@Thickness 1.57 mm
 90 - 110

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 82.7 MPa

@Thickness 1.57 mm
 12000 psi

@Thickness 0.0620 in
 CW; ASTM D638
96.5 MPa

@Thickness 1.57 mm
 14000 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 7.24 GPa

@Thickness 1.57 mm
 1050 ksi

@Thickness 0.0620 in
 CW; ASTM D229
8.96 GPa

@Thickness 1.57 mm
 1300 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 103 MPa

@Thickness 1.57 mm
 15000 psi

@Thickness 0.0620 in
 CW; ASTM D790
138 MPa

@Thickness 1.57 mm
 20000 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 207 MPa

@Thickness 12.7 mm
 30000 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 88.3 MPa

@Thickness 15.7 mm
 12800 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 0.240 J/cm

@Thickness 12.7 mm
 0.450 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
0.294 J/cm

@Thickness 12.7 mm
 0.550 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 19.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 10.6 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 15.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 8.33 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 130 °C
266 °F
Flammability, UL94 HB

@Thickness 1.57 mm
 HB

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Constant 6.1

@Thickness 1.57 mm
 6.1

@Thickness 0.0620 in
 Permittivity, Cond D-24/23; ASTM D150
Dielectric Strength 23.6 kV/mm

@Thickness 1.57 mm
 600 kV/in

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S.T.
27.6 kV/mm

@Thickness 1.57 mm
 700 kV/in

@Thickness 0.0620 in
 Cond A; ASTM D229 S.T.
Dielectric Breakdown 10000 V

@Thickness 1.57 mm
 10000 V

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S/S
40000 V

@Thickness 1.57 mm
 40000 V

@Thickness 0.0620 in
 Cond A; ASTM D229 S/S
Dissipation Factor 0.050

@Thickness 1.57 mm
 0.050

@Thickness 0.0620 in
 Cond D-24/23; ASTM D150
Arc Resistance 110 sec

@Thickness 3.17 mm
 110 sec

@Thickness 0.125 in
 ASTM D495
Comparative Tracking Index 200 V

@Thickness 3.17 mm
 200 V

@Thickness 0.125 in
 ASTM D3638
Descriptive Properties Value Comments
Bond Strength 1000 lb
0.5", ASTM D229
Color Natural, Black
Users viewing this material also viewed the following: