SABIC Innovative Plastics LNP THERMOCOMP Lexan_JK500 PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP Lexan_JK500 PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
10% GR, ECO conforming FR, PC+ABS for thinwall molding applications.
Physical Properties Metric English Comments
Specific Gravity 1.27 g/cc
1.27 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0010 - 0.0025 cm/cm

@Thickness 3.20 mm
 0.0010 - 0.0025 in/in

@Thickness 0.126 in
 SABIC Method
Linear Mold Shrinkage, Transverse 0.0030 - 0.0045 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.0045 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 20 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 20 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 ASTM D1238
33 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 33 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 68.0 MPa
9860 psi
Type I, 5 mm/min; ASTM D638
70.0 MPa
10200 psi
5 mm/min; ISO 527
Tensile Strength, Yield 68.0 MPa
9860 psi
Type I, 5 mm/min; ASTM D638
70.0 MPa
10200 psi
5 mm/min; ISO 527
Elongation at Break 2.1 %
2.1 %
5 mm/min; ISO 527
5.0 %
5.0 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 2.1 %
2.1 %
5 mm/min; ISO 527
5.0 %
5.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 4.82 GPa
699 ksi
5 mm/min; ASTM D638
5.25 GPa
761 ksi
1 mm/min; ISO 527
Flexural Strength 115 MPa
16700 psi
2 mm/min; ISO 178
117 MPa
17000 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 115 MPa
16700 psi
2 mm/min; ISO 178
Flexural Modulus 4.34 GPa
629 ksi
1.3 mm/min, 50 mm span; ASTM D790
4.59 GPa
666 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.580 J/cm
1.09 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.15 J/cm
5.90 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 21.0 kJ/m²
9.99 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 13.0 J

@Temperature 23.0 °C
 9.59 ft-lb

@Temperature 73.4 °F
 ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 43.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 23.9 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
43.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
 24.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 40.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
83.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
 46.1 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 96.0 °C

@Thickness 3.20 mm
 205 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 88.0 °C

@Thickness 3.20 mm
 190 °F

@Thickness 0.126 in
 unannealed; ASTM D648
93.0 °C

@Thickness 6.40 mm
 199 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 100 °C
212 °F
Rate B/120; ISO 306
110 °C
230 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 V-0

@Thickness 0.990 mm
 V-0

@Thickness 0.0390 in
 UL 94