Overview of materials for Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler". Specific grades with glass content between 15% and 24% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.30 - 1.58 g/cc
0.0470 - 0.0571 lb/in³
Average value: 1.46 g/cc Grade Count:17
Filler Content 15.0 - 20.0 %
15.0 - 20.0 %
Average value: 17.5 % Grade Count:6
Water Absorption 0.0100 - 0.0200 %
0.0100 - 0.0200 %
Average value: 0.0183 % Grade Count:6
0.0300 - 0.0300 %

@Temperature -17.8 - -17.8 °C
0.0300 - 0.0300 %

@Temperature 0.000 - 0.000 °F
Average value: 0.0300 % Grade Count:1
Water Absorption at Saturation 0.0200 %
0.0200 %
Average value: 0.0200 % Grade Count:6
Linear Mold Shrinkage 0.00100 - 0.00700 cm/cm
0.00100 - 0.00700 in/in
Average value: 0.00342 cm/cm Grade Count:11
Linear Mold Shrinkage, Transverse 0.00400 - 0.0100 cm/cm
0.00400 - 0.0100 in/in
Average value: 0.00650 cm/cm Grade Count:4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 100 - 118
100 - 118
Average value: 104 Grade Count:4
Hardness, Rockwell R 87.0 - 121
87.0 - 121
Average value: 110 Grade Count:3
Tensile Strength, Ultimate 86.0 - 130 MPa
12500 - 18900 psi
Average value: 111 MPa Grade Count:16
Elongation at Break 1.00 - 2.90 %
1.00 - 2.90 %
Average value: 1.77 % Grade Count:16
Modulus of Elasticity 5.00 - 9.65 GPa
725 - 1400 ksi
Average value: 7.89 GPa Grade Count:11
Flexural Yield Strength 113 - 200 MPa
16400 - 29000 psi
Average value: 160 MPa Grade Count:16
Flexural Modulus 5.10 - 9.31 GPa
740 - 1350 ksi
Average value: 7.66 GPa Grade Count:17
Izod Impact, Notched 0.427 - 1.92 J/cm
0.800 - 3.60 ft-lb/in
Average value: 0.771 J/cm Grade Count:11
Izod Impact, Unnotched 2.14 - 6.90 J/cm
4.00 - 12.9 ft-lb/in
Average value: 3.23 J/cm Grade Count:8
Izod Impact, Notched (ISO) 5.20 - 35.0 kJ/m²
2.47 - 16.7 ft-lb/in²
Average value: 10.8 kJ/m² Grade Count:7
Izod Impact, Unnotched (ISO) 35.0 - 45.0 kJ/m²
16.7 - 21.4 ft-lb/in²
Average value: 38.3 kJ/m² Grade Count:3
Charpy Impact Unnotched 3.20 - 4.80 J/cm²
15.2 - 22.8 ft-lb/in²
Average value: 3.73 J/cm² Grade Count:3
Charpy Impact, Notched 0.500 - 1.40 J/cm²
2.38 - 6.66 ft-lb/in²
Average value: 0.800 J/cm² Grade Count:3
Thermal Properties Metric English Comments
CTE, linear 23.4 - 30.0 µm/m-°C
13.0 - 16.7 µin/in-°F
Average value: 26.4 µm/m-°C Grade Count:4
20.0 - 20.0 µm/m-°C

@Temperature 100 - 200 °C
11.1 - 11.1 µin/in-°F

@Temperature 212 - 392 °F
Average value: 20.0 µm/m-°C Grade Count:1
CTE, linear, Transverse to Flow 53.0 - 63.4 µm/m-°C
29.4 - 35.2 µin/in-°F
Average value: 57.1 µm/m-°C Grade Count:3
90.0 - 90.0 µm/m-°C

@Temperature 100 - 200 °C
50.0 - 50.0 µin/in-°F

@Temperature 212 - 392 °F
Average value: 90.0 µm/m-°C Grade Count:1
Melting Point 278 - 280 °C
532 - 536 °F
Average value: 280 °C Grade Count:4
Deflection Temperature at 0.46 MPa (66 psi) 246 - 280 °C
475 - 536 °F
Average value: 262 °C Grade Count:3
Deflection Temperature at 1.8 MPa (264 psi) 190 - 265 °C
374 - 509 °F
Average value: 249 °C Grade Count:16
Flammability, UL94 V-0
V-0
Grade Count:13
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+14 - 2.20e+16 ohm-cm
1.00e+14 - 2.20e+16 ohm-cm
Average value: 8.01e+15 ohm-cm Grade Count:8
Surface Resistance 1.00e+15 - 1.00e+16 ohm
1.00e+15 - 1.00e+16 ohm
Average value: 4.56e+15 ohm Grade Count:5
Insulation Resistance 1.00e+13 - 1.00e+13 ohm

@Temperature 90.0 - 90.0 °C
1.00e+13 - 1.00e+13 ohm

@Temperature 194 - 194 °F
Average value: 1.00e+13 ohm Grade Count:1
Dielectric Constant 3.20 - 3.60
3.20 - 3.60
Average value: 3.41 Grade Count:6
Dielectric Strength 13.8 - 24.0 kV/mm
350 - 610 kV/in
Average value: 16.0 kV/mm Grade Count:6
Dissipation Factor 0.00100 - 0.00500
0.00100 - 0.00500
Average value: 0.00186 Grade Count:6
Arc Resistance 100 - 120 sec
100 - 120 sec
Average value: 110 sec Grade Count:4
Processing Properties Metric English Comments
Processing Temperature 20.0 - 340 °C
68.0 - 644 °F
Average value: 215 °C Grade Count:5
Die Temperature 310 - 330 °C
590 - 626 °F
Average value: 320 °C Grade Count:4
Melt Temperature 20.0 - 340 °C
68.0 - 644 °F
Average value: 292 °C Grade Count:12
Mold Temperature 130 - 177 °C
266 - 350 °F
Average value: 154 °C Grade Count:8
Drying Temperature 80.0 - 149 °C
176 - 300 °F
Average value: 139 °C Grade Count:11
Moisture Content 0.0200 - 0.0400 %
0.0200 - 0.0400 %
Average value: 0.0320 % Grade Count:10
Injection Pressure 50.0 - 103 MPa
7250 - 15000 psi
Average value: 82.1 MPa Grade Count:11