Special Metals NILO® Alloy 36 Low-Expansion Alloy
| Category | Metal , Superalloy , Iron Base |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | NILO® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals NILO® Alloy 36 Low-Expansion Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Inflection point 220°C. A nickel-iron low-expansion alloy containing 36% nickel. It maintains nearly constant dimensions over the range of normal atmospheric temperatures, and has a low coefficient of expansion from cryogenic temperatures to about 500°F (260°C). The alloy also retains good strength and toughness at cryogenic temperatures. Used for standards of length, measuring devices, laser components, bi-metal thermostat strip, thermostat rods, and tanks and piping for storing and transporting liquefied gases. Standard product forms are round, extruded section, plate, sheet, strip, tube, pipe, and wire.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.11 g/cc | 0.293 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 490 MPa | 71100 psi | Annealed prior to test |
| 430 MPa @Temperature 300 °C |
62400 psi @Temperature 572 °F |
Annealed prior to test | |
| Tensile Strength, Yield | 240 MPa @Strain 0.200 % |
34800 psi @Strain 0.200 % |
Annealed prior to test |
| 110 MPa @Strain 0.200 %, Temperature 300 °C |
16000 psi @Strain 0.200 %, Temperature 572 °F |
Annealed prior to test | |
| Elongation at Break | 42 % | 42 % | Annealed prior to test. |
| 50 % @Temperature 300 °C |
50 % @Temperature 572 °F |
Annealed prior to test. |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 1.50 µm/m-°C @Temperature 20.0 - 100 °C |
0.833 µin/in-°F @Temperature 68.0 - 212 °F |
|
| 2.60 µm/m-°C @Temperature 20.0 - 200 °C |
1.44 µin/in-°F @Temperature 68.0 - 392 °F |
||
| Thermal Conductivity | 10.0 W/m-K | 69.4 BTU-in/hr-ft²-°F | |
| Melting Point | 1430 °C | 2610 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.10 % | <= 0.10 % | |
| Chromium, Cr | <= 0.50 % | <= 0.50 % | |
| Cobalt, Co | <= 1.0 % | <= 1.0 % | |
| Iron, Fe | 60 % | 60 % | As remainder |
| Manganese, Mn | <= 0.60 % | <= 0.60 % | |
| Molybdenum, Mo | <= 0.50 % | <= 0.50 % | |
| Nickel, Ni | 35 - 38 % | 35 - 38 % | |
| Phosphorous, P | <= 0.025 % | <= 0.025 % | |
| Silicon, Si | <= 0.35 % | <= 0.35 % | |
| Sulfur, S | <= 0.025 % | <= 0.025 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.0000800 ohm-cm | 0.0000800 ohm-cm |
Users viewing this material also viewed the following:
- 3M Scotch-Grip™/Fastbond™ 5298 Industrial Adhesive (discontinued **)
- Zyvex Performance Materials Arovex™ HT 250 Nano-Engineered Composite Prepreg System
- Dow Corning SILASTIC® LSR 9390-60 PARTS A&B
- Bohler-Uddeholm BÖHLER W302 SUPERIOR® Premium H13 Tool Steel
- Asahi Kasei Leona® 1500 Nylon 66
- Asahi Kasei Xyron® 100V Modified Polyphenylene Ether
- Bisalloy Steels BisPlate 80 Thickness >80-100 mm
- Arlon LW201C##FR-P1 0.020" (0.508 mm) Self-Fusing Silicone Tape (Triangular, Unsupported)
- TSE Industries Millathane® 97 Millable Polyester Polyurethane Rubber, 10.0 PHR Wacker HDK N20 Filler
- 3M Dyneon™ CC203 Custom Fluoropolymer Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved