SABIC Innovative Plastics LNP COLORCOMP AX03654 ABS (Asia Pacific)

Category	Polymer , Thermoplastic , ABS Polymer
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP Colorcomp
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP COLORCOMP AX03654 ABS (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP COLORCOMP* AX03654 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Unfilled Custom Color. Added features of this material include: Flame Retardant.

Physical Properties	Metric	English	Comments
Density	1.16 g/cc	0.0419 lb/in³	ASTM D792
	1.16 g/cc	0.0419 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm @Time 86400 sec	0.0050 - 0.0070 in/in @Time 24.0 hour	ASTM D955
	0.0050 - 0.0070 cm/cm @Time 86400 sec	0.0050 - 0.0070 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.0050 - 0.0070 cm/cm @Time 86400 sec	0.0050 - 0.0070 in/in @Time 24.0 hour	ASTM D955
	0.0050 - 0.0070 cm/cm @Time 86400 sec	0.0050 - 0.0070 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	30.0 MPa	4350 psi	ASTM D638
	31.0 MPa	4500 psi	ISO 527
Tensile Strength, Yield	38.0 MPa	5510 psi	ISO 527
	39.0 MPa	5660 psi	ASTM D638
Elongation at Break	13.6 %	13.6 %	ASTM D638
	15.3 %	15.3 %	ISO 527
Elongation at Yield	2.0 %	2.0 %	ISO 527
	2.1 %	2.1 %	ASTM D638
Tensile Modulus	2.39 GPa	347 ksi	1 mm/min; ISO 527
	2.44 GPa	354 ksi	50 mm/min; ASTM D638
Flexural Strength	65.0 MPa	9430 psi	ASTM D790
	65.0 MPa	9430 psi	ISO 178
Flexural Modulus	2.31 GPa	335 ksi	ISO 178
	2.39 GPa	347 ksi	ASTM D790
Izod Impact, Notched	1.70 J/cm	3.18 ft-lb/in	ASTM D256
Izod Impact, Unnotched	10.68 J/cm	20.01 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	11.0 kJ/m²	5.23 ft-lb/in²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	39.0 kJ/m²	18.6 ft-lb/in²	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	72.0 °C	162 °F	Flatw 80104 sp=64mm; ISO 75/Af
	72.0 °C @Thickness 3.20 mm	162 °F @Thickness 0.126 in	unannealed; ASTM D648