Lehmann & Voss LUVOCOM® 21-8113 Polyamide 6/6T, with carbon fiber, lubricant modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 21-8113 Polyamide 6/6T, with carbon fiber, lubricant modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Dynamic stressed parts at high movement velocity.Improved friction and wear behaviour. Emergency running property.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ISO 1183 |
| Water Absorption | <= 0.30 % | <= 0.30 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 120 MPa | 17400 psi | |
| Elongation at Yield | 1.1 % | 1.1 % | |
| 1.4 % | 1.4 % | flexural | |
| Modulus of Elasticity | 13.0 GPa | 1890 ksi | |
| Flexural Strength | 180 MPa | 26100 psi | |
| Flexural Modulus | 11.0 GPa | 1600 ksi | |
| Charpy Impact Unnotched | 1.70 J/cm² | 8.09 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 135 °C | 275 °F | |
| 160 °C | 320 °F | short term |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm | |
| Insulation Resistance | <= 1.00e+9 ohm | <= 1.00e+9 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 330 °C | 626 °F | mass temp |
| Nozzle Temperature | 330 - 340 °C | 626 - 644 °F | |
| Zone 1 | 300 - 340 °C | 572 - 644 °F | |
| Zone 2 | 310 - 340 °C | 590 - 644 °F | |
| Zone 3 | 320 - 340 °C | 608 - 644 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 80.0 °C @Time 21600 - 57600 sec |
176 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 110 °C @Time 14400 - 21600 sec |
230 °F @Time 4.00 - 6.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | dark grey |
Users viewing this material also viewed the following:
- Nyco M1250 AS WOLLASTOCOAT® Wollastonite
- Omni Plastics OmniTuff™ CPP TF30 Copolymer Polypropylene Talc Filled
- S&E Specialty Polymers GA-509ORLT PVC
- Osprey Metals 304L Stainless Steel Powder (Grade 90% - 22)
- Guarniflon PTFE G800 Polytetrafluoroethylene
- Solvay Chemicals Strontium carbonate standard powder
- Zeon Chemicals Quintone® E200SN Aliphatic Hydrocarbon Resin
- Arlon 28751R015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Axiall 19854 Wire & Cable Flexible PVC
- Bulk Molding Compounds BMC 1423 Wear Resistant, Electrical Grade
Copyright © lookpolymers.com All Rights Reserved