SABIC Innovative Plastics Cycolac® MG37CR ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycolac®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycolac® MG37CR ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High performance, injection molding ABS. Overall balance of physical properties, good processability and chemical resistance.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D 792
Viscosity 255000 cP

@Temperature 240 °C
255000 cP

@Temperature 464 °F
melt; 1000 sec-1; ASTM D 3825
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 4.4 g/10 min

@Load 3.80 kg,
Temperature 230 °C
4.4 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D 1238
16 g/10 min

@Load 10.0 kg,
Temperature 220 °C
16 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 32.0 MPa
4640 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 41.0 MPa
5950 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 25 %
25 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 2.1 %
2.1 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 2.27 GPa
329 ksi
5 mm/min; ASTM D 638
Flexural Yield Strength 68.0 MPa
9860 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.34 GPa
339 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 3.47 J/cm

@Temperature 23.0 °C
6.50 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Impact Test 34.0 J

@Temperature 23.0 °C
25.1 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 77.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 73.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 98.0 °C

@Thickness 3.20 mm
208 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C

@Thickness 3.20 mm
185 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 101 °C
214 °F
Rate B/50; ASTM D 1525
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.52 mm
HB

@Thickness 0.0598 in
UL 94
Electrical Properties Metric English Comments
Arc Resistance 60 - 120 sec
60 - 120 sec
Tungsten, PLC code 6; ASTM D 495
Comparative Tracking Index 400 - 600 V
400 - 600 V
PLC code 1; UL 746A
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
PLC code 3; UL 746A
High Amp Arc Ignition, HAI 15 - 30 arcs
15 - 30 arcs
surface, PLC code 3; UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
PLC code 3; UL 746A