DuPont Performance Polymers Crastin® CE2055 NC010 Polybutylene Terephthalate (PBT)

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer	DuPont Performance Polymers
Trade Name	Crastin®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Crastin® CE2055 NC010 Polybutylene Terephthalate (PBT).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Unreinforced Low Viscosity Polybutylene Terephthalate Crastin CE2055 NC010 is an unreinforced low viscosity polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.31 g/cc	0.0473 lb/in³	ISO 1183
Linear Mold Shrinkage, Flow	0.020 cm/cm	0.020 in/in	ISO 294-4 2577
Linear Mold Shrinkage, Transverse	0.018 cm/cm	0.018 in/in	ISO 294-4 2577

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	60.0 MPa	8700 psi	ISO 527-1/-2
Elongation at Break	13 %	13 %	Nominal; ISO 527-1/-2
Elongation at Yield	10 %	10 %	ISO 527-1/-2
Tensile Modulus	2.60 GPa	377 ksi	ISO 527-1/-2
Flexural Strength	82.0 MPa	11900 psi	ISO 178
Izod Impact, Notched (ISO)	3.90 kJ/m²	1.86 ft-lb/in²	ISO 180/1A
Charpy Impact, Notched	0.350 J/cm²	1.67 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	225 °C	437 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	150 °C	302 °F	ISO 75-1/-2
	184 °C	363 °F	annealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	55.0 °C	131 °F	ISO 75-1/-2
	73.0 °C	163 °F	annealed; ISO 75-1/-2
Vicat Softening Point	175 °C	347 °F	50°C/h 50N; ISO 306

Descriptive Properties	Value	Comments
Delivery Form	Pellets
Part Marking Code	>PBT<	ISO 11469
Processing	Injection Moulding
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	PBT