- Polymer Property : Tensile Strength at Break = 32.0 MPa
Polymer Property : Tensile Strength at Break = 32.0 MPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 32.0 MPa | 4640 psi | Type I, 5 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Cycolac® MG37CR ABS (Asia Pacific) High performance, injection molding ABS. Overall balance of physical properties, good processability and chemical resistance.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | 50 mm/min; ASTM D638 |
| Ovation Polymers Nemcon™ H ABS DP116P ABS ABS-Thermally conducting, electrically insulating grade with high HDT and improved processability.Information provided by Ovation Polymers |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Geloy XTWE270M ASA+SAN (Asia Pacific) Excellent weatherability, good flow/aesthetics and good impact.Profile co-extrusion grade over ABS, PVC or other compatible polymers. XTWE270M is available in various colours.This data was supplied.. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP Faradex AS0039 ABS (Europe-Africa-Middle East) LNP* Faradex* AS0039 is a compound based on Acrylonitrile Butadiene Styrene resin containing Flame Retardant, Stainless Steel Fiber. Added features of this material include: EMI/RFI Shielding.This .. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP AI001XXH ABS LNP* Lubricomp* AI001XXH is a compound based on ABS containing 2% Silicone. Characteristics of this grade are: Healthcare and Internally Lubricated. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing 15% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS (Europe-Africa-Middle East) LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| Petromont 2100 Medium Density Polyethylene Resin Petromont HDPE 2100 is a medium density polyethylene blown film resin produced using the UNIPOL™ Process. This resin is designed specifically for blown film made by co-extrusion. It is commonly use.. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS LNP LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS LNP LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing 10% PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP AL002 ABS (Europe-Africa-Middle East) LNP* LUBRICOMP* AL002 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| Braskem BS 002J HDPE Blow Molding Polyethylene
(discontinued **) Applications: Bottles up to 60 liters with high ESCR; bottles for surface-active agents. Information provided by Braskem |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | DIN 53504 |
| Huntsman IROGRAN® A 80 P 5039 TPU-Polyether Excellent resistance to hydrolysis and microbial attack. Suggested for injection molding and extrusion.Information provided by Huntsman |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | Type I, 50 mm/min; ASTM D 638 |
| SABIC Innovative Plastics Noryl RF1132 PPE+PP PPE+PP blend for high frequency applications. Good heat resistance and low DK.This data was supplied by SABIC-IP for the Americas region. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | Type I, 5 mm/min; ASTM D638 |
| SABIC Innovative Plastics LNP STAT-KON FD000 PE LNP* STAT-KON* FD000 is an unfilled Polyethylene. Added feature of this grade is: Electrically Conductive. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Stat-loy K3000 Acetal Copoly LNP* Stat-loy* K3000 is a compound based on Acetal Copolymer resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americas regi.. |
|||
| Tensile Strength at Break | >= 32.0 MPa | >= 4640 psi | ISO R 527 |
| Stir SpA Giesse RSA/12 (PVC) Application: Blow molding very high shock resistanceInformation provided by STIR SpA |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527 |
| Chi Mei Polylac® PA-709 ABS Super impact |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527 |
| Chi Mei Polylac® PA-737 ABS - High Flow High flow, medium impact |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | 50 mm/min; ISO 527 |
| Chi Mei Polylac® PA-746 ABS - High Flow High flow, medium impact |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | Conditioned 15 days at 23°C - 50% RH; ASTM D638 |
| Arkema Group Pebax® 2533 SA 01 MED Polyether Block Amide (PEBA) Polyether block amide PEBAX® 2533 SA 01 MED is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This grade offers the highest quality and it is specially designed to meet t.. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| Azdel SuperLite® SL550900-100 PP Resin Matrix / 55% Glass Fiber (2 mm Molded Thickness) AZDEL SuperLite® SL550900-100 is a low pressure, thermoformable, thermoplastic composite of polypropylene and long chopped glass fibers. Usually combined with outer layers as needed for the applic.. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| Aclo Accutech Polypropylene Homopolymer HP0339M10CL Mica Reinforced Coupled |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | Conditioned; ISO R 527 |
| Addiplast Addilene H 490 S Flame Retardant Polypropylene Flame retardant, unreinforced, with halogensInformation provided by Addiplast. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | |
| AorTech Biomaterials ECSil™ 75A Biomedical Carbonate Silicone Pellets Elast-Eon™ Carbonate Silicone (ECSil™) is a family of next generation biomedical polymers. ECSil™ is finding strong interest in cardiac pacing leads, orthopaedics, spinal discs, and generally an.. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | DIN EN ISO 527-3 |
| 3M Dyneon™ TF 2053Z PTFE Fine Powder Dyneon™ TF 2053 Z PTFE is an ideal grade for extrusion of tubing and cables requiring only moderately high reduction ratio.Product Features:Processable by standard paste extrusion methods Good over.. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | STN EN ISO 527-2 |
| Plastcom SLOVALEN PH 51 T 15 Polypropylene Homopolymer, 15% Mineral Filled FeaturesModified homopolymer PP for injection moulding with the content of 15% mineral filler. Increased rigidity, strength and thermal use up to 130°C. Decreased shrinkage. General application .. |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO R 527 |
| Fainplast Compounds RE 430 Rigid PVC, Extrusion Electric channels |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ISO R 527 |
| Fainplast Compounds RE 230/D Rigid PVC, Extrusion Electric channels |
|||
| Tensile Strength at Break | 32.0 MPa | 4640 psi | ASTM D638 |
| Braskem BU 004 HDPE Blow Molding Polyethylene Applications: Bottles for food products, lubricating and cooking oil; toys; bottler for surface-active agents; sheets. Information provided by Braskem |
|||