- RheTech Products FRP257-00 32% Talc Reinforced Polypropylene Copolymer, Flame Retardant, Natural
RheTech Products FRP257-00 32% Talc Reinforced Polypropylene Copolymer, Flame Retardant, Natural
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products FRP257-00 32% Talc Reinforced Polypropylene Copolymer, Flame Retardant, Natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Electrical component housingsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 32 % | 32 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
7.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 72 | 72 | ASTM D2240 |
| Tensile Strength at Break | 20.7 MPa | 3000 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 3.03 GPa | 440 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm @Temperature 23.0 °C |
0.800 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 5.08 J | 3.75 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 191 - 199 °C | 375 - 390 °F | |
| Middle Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Front Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Nozzle Temperature | 204 °C | 400 °F | |
| Mold Temperature | 23.9 - 35.0 °C | 75.0 - 95.0 °F | |
| Drying Temperature | 51.7 - 65.6 °C | 125 - 150 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 2.76 - 8.27 MPa | 400 - 1200 psi | |
| Hold Pressure | 2.07 - 6.89 MPa | 300 - 1000 psi | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi |
Users viewing this material also viewed the following:
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with Plasticizer SC
- Huntsman IROGRAN® A 85 P 5004 TPU-Polyether
- Flint Hills P9R6K-054A Random Copolymer Polypropylene
- LTL Color Compounds ColorRxâ„¢ PE3-0202ARX Biocompatible, Antimicrobial LDPE
- Sylvin Technologies 6034-85 PVC Wire/Cable Compound
- Dow FLEXOMER™ GRSN-1539 NT 7 Very Low Density Polyethylene (VLDPE) Resin
- Eurostar Star L PA66 D61 PA66, Injection Molded
- Ascend Performance Materials Vydyne® 49H NT Nylon 66, Impact Modified, Conditioned
- M. Holland Company IS325 Polystyrene, High Impact (discontinued **)
Copyright © lookpolymers.com All Rights Reserved