- RheTech Products CS30P100-01UV 30% Ceramic Sphere Reinforced Polypropylene, UV Stabilized, Black
RheTech Products CS30P100-01UV 30% Ceramic Sphere Reinforced Polypropylene, UV Stabilized, Black
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | RheTech Products |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RheTech Products CS30P100-01UV 30% Ceramic Sphere Reinforced Polypropylene, UV Stabilized, Black.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Consumer goodsHousingsInjection molding conditions reported in table.Information provided by RheTech Products.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | 23/23°C; ASTM D792 |
| Filler Content | 30 % | 30 % | ASTM D5630 |
| Linear Mold Shrinkage | 0.0105 cm/cm | 0.0105 in/in | ASTM D955 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 73 | 73 | ASTM D2240 |
| Tensile Strength at Break | 22.1 MPa | 3200 psi | 2 in/min; ASTM D638 |
| Flexural Modulus | 1.72 GPa | 250 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Temperature 23.0 °C |
0.500 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Gardner Impact | 0.790 J | 0.583 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.6 °C | 195 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.4 °C | 130 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 232 °C | 400 - 450 °F | |
| Middle Barrel Temperature | 210 - 238 °C | 410 - 460 °F | |
| Front Barrel Temperature | 216 - 243 °C | 420 - 470 °F | |
| Nozzle Temperature | 221 - 232 °C | 430 - 450 °F | |
| Mold Temperature | 26.7 - 48.9 °C | 80.0 - 120 °F | |
| Drying Temperature | 65.6 - 82.2 °C | 150 - 180 °F | |
| Dry Time | 1 - 2 hour | 1 - 2 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % | Recommended |
| Injection Pressure | 55.2 - 103 MPa | 8000 - 15000 psi | |
| Hold Pressure | 27.6 - 51.7 MPa | 4000 - 7500 psi | |
| Back Pressure | 0.345 - 1.03 MPa | 50.0 - 150 psi |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 121 PC (Asia Pacific)
- NOVA Chemicals Novapol® TR-0338-UI Hexene MDPE Rotational Molding Resin
- DSM Akulon® S223-E Nylon 66 (European and Asian Grade) (Dry) (discontinued **)
- LyondellBasell Petrothene® LT570401 High Density Polyethylene
- Huntsman DT 3355 Matting Agent
- Ipiranga Petrochem PH 0241 Polypropylene
- Lehmann & Voss LUVOCOM® 1104-7598 Polyether ketone, with carbon fiber, PTFE, lubricant modified
- Samsung Cheil Industries Infino® MKD-1016 PA, 55% Glass Filled
- A. Schulman POLYFORT™ FPP 3460 Glass-Mineral Hybrid Filled Copolymer
- Zylog Hipolyene® 1048 X1 Thermoplastic Polyolefin & PP Compound
Copyright © lookpolymers.com All Rights Reserved