- Ravago Manufacturing Americas Hylon® N2033HL Nylon 6 (Cond)
Ravago Manufacturing Americas Hylon® N2033HL Nylon 6 (Cond)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Heat Stabilized |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylon® N2033HL Nylon 6 (Cond).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | DAM; ASTM D792 |
| Water Absorption | 1.1 % | 1.1 % | 24 hrs, DAM; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | 0.125 in, DAM; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 127 MPa | 18400 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
| Flexural Modulus | 5.12 GPa | 743 ksi | ASTM D790 |
| Izod Impact, Notched | 2.35 J/cm | 4.40 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB | HB | 0.0590 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 254 - 277 °C | 490 - 530 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.18 % | 0.18 % | |
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |
| Screw Speed | 50 - 120 rpm | 50 - 120 rpm |
Users viewing this material also viewed the following:
- Multibase SILASTIC® Q7-4720 Dow-Corning Biomedical Grade ETR Elastomer
- Chevron Phillips MarFlex® ER3341 Polyethylene; Masterbatch (discontinued **)
- Plenco 504 Black (COM) Heat Resistant Mineral/Cellulose Filled Phenolic Molding Compound (discontinued **)<
- Hong Kun Group HBCD Flame Retardant
- LG Chemical LUMID GP2151AF PA6+GF15%, Flame Retardant
- Haynes 214® alloy, 20% cold reduction, 925°C for 5 minutes
- SABIC Innovative Plastics ULTEM 1010 PEI (Asia Pacific)
- Teknor Apex Chemlon® 267 Nylon 6, Impact Modified
- Zircar Refractory Composites RSBD-HD ALUMINA-SILICA INSULATION
- Trelleborg R395 Natural Rubber Polyisoprene
Copyright © lookpolymers.com All Rights Reserved