| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 127 MPa | 18400 psi | ASTM D638 |
| Ravago Manufacturing Americas Hylon® N2033HL Nylon 6 (Cond) Information provided by Ravago. |
|||
| Tensile Strength, Yield | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP LUBRICOMP DFL38 PC LNP* Lubricomp* DFL-4038 is a Polycarbonate containing 40% Glass Fiber, 15% PTFE. Added features include: Internally Lubricated. |
|||
| Tensile Strength, Yield | 127 MPa @Thickness 3.20 mm |
18500 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| LG Chemical LUMID GP2130A(W) PA6+GF13%, General Purpose Feature: Injection Molding, PA6+GF13%, General PurposeApplication: Automotive PartsCAS No. 25038-54-4 and 65997-17-3Information provided by LG Chemical |
|||
| Tensile Strength, Yield | 127 MPa @Thickness 3.20 mm |
18500 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| LG Chemical LUMID GP2259AFL PA6+GF25%, Flame Retardant Feature: Injection Molding, PA6+GF25%, Flame RetardantApplication: IT/OA (Connector)CAS No. 25038-54-4, 65997-17-3, 1163-19-5, 1309-64-4 and 138265-88-0Information provided by LG Chemical |
|||
| Tensile Strength, Yield | 127 MPa @Thickness 3.20 mm |
18500 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| LG Chemical LUMID HI2202B(W) PA66+GF20%, High Impact Feature: Injection Molding, PA66+GF20%, High ImpactApplication: Automotive (Covers)CAS No. 25038-54-4, 9010-79-1 and 65997-17-3Information provided by LG Chemical |
|||
| Tensile Strength, Yield | 127 MPa @Thickness 3.20 mm |
18500 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| LG Chemical LUMID LW4403A(W) PA66+GF/MF40%, Low Warpage Feature: Injection Molding, PA66+GF/MF40%, Low WarpageApplication: Automotive (Timing Belt Cover)CAS No. 25038-54-4, 13983-17-0 and 65997-17-3Information provided by LG Chemical |
|||
| Tensile Strength, Yield | 127 MPa @Thickness 3.20 mm |
18500 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| LG Chemical LUMID SG4389B PA66+GF/MF38% Feature: Injection Molding, PA66+GF/MF38%Application: Automotive (Fan & Shroud)CAS No. 32131-17-2, 25038-54-4, 65997-17-3 and 14807-96-6Information provided by LG Chemical |
|||
| Tensile Strength, Yield | 127 MPa | 18400 psi | ASTM D638 |
| LG Chemical LUPOY GP-2301F General Purpose Modified PC, 30% Glass Fiber Reinforced, Flame Retardant Among the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.Applications:Automotive: Automotive.. |
|||
| Tensile Strength, Yield | 127 MPa | 18400 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp KCL34 Acetal Copoly (Asia Pacific) LNP* Lubricomp* KCL34 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data .. |
|||
| Tensile Strength, Yield | 127 MPa | 18400 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP OCP36A PPS - Branched LNP* LUBRICOMP* OCP36A is a compound based on PPS - Branched resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this material include: Wear Resistant, Electrically Conductive. |
|||
| Tensile Strength, Yield | 127 MPa | 18400 psi | ASTM D638 |
| SABIC Innovative Plastics LNP LUBRICOMP OCP36A PPS - Branched (Asia Pacific) LNP* Lubricomp* OCL-4536 is a compound based on PPS - Branched resin containing PTFE, Carbon Fiber, Silicone. Added features of this material include: Internally Lubricated, Electrically Conductive.. |
|||
| Tensile Strength, Yield | 127 MPa | 18400 psi | SABIC - Japan Method |
| SABIC Innovative Plastics ULTEM JD7101 PEI (Asia Pacific) |
|||
| Tensile Strength, Yield | 127 MPa | 18400 psi | SABIC - Japan Method |
| SABIC Innovative Plastics Ultem JD7902 PEI (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
| Tensile Strength, Yield | 127 MPa | 18400 psi | 5 mm/min; ISO 527 |
| SABIC Innovative Plastics LNP STAT-LOY ZF3021 PPE+PS (Europe-Africa-Middle East) LNP* STAT-LOY* ZF3021 is a compound based on PPE + PS Blend resin containing Glass Fiber. Added features include Antistatic, Flame Retardant. |
|||
| Tensile Strength, Yield | 127 MPa | 18500 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® VB-5300G PBT, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 127 MPa | 18500 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® VB-5300GS PBT, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 127 MPa | 18500 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® VB-5302GR PBT, 30% Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 127 MPa | 18500 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® VB-5400G PBT, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 127 MPa | 18500 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® XP-2130A PPS Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 127 MPa | 18500 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® XP-4240 PPS/PPA Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 127 MPa | 18500 psi | ASTM D638 |
| Samyang Trirex® 3500G30 Polycarbonate, 30% Glass Reinforced TRIREX® polycarbonate resins offer superior transparency, mechanical properties, good dimensional stability and high electrical performance, which allows it to be widely used for electrical, elec.. |
|||
| Tensile Strength, Yield | 127 MPa | 18400 psi | ASTM D 638 |
| SABIC Innovative Plastics LNP Lubricomp KCL34 Acetal Copoly LNP* Lubricomp* KCL34 is a compound based on Acetal Copolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive.This data .. |
|||
| Tensile Strength, Yield | 127 MPa | 18500 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® VB-5400G PBT, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 127 MPa | 18400 psi | SABIC - Japan Method |
| SABIC Innovative Plastics NORYL GTX APS440 PPE+PPS (Asia Pacific) PPE+PPS, GF40%, FR V-0 |
|||
| Tensile Strength, Yield | 127 MPa | 18500 psi | ASTM D638 |
| Cheng Yu Plastic T885GV3 Flame Retardant PBT, 30% Glass Fiber |
|||
| Tensile Strength, Yield | 127 MPa | 18500 psi | ASTM D638 |
| Cheng Yu Plastic T890G3 PBT, 30% Glass Fiber |
|||
| Tensile Strength, Yield | 127 MPa | 18400 psi | ASTM D638 |
| Ashley Polymers Ashlene® 79MGS Nylon 6, 40% Glass Mineral reinforced A 40% glass mineral reinforced Nylon 6 with good dimensional stability, stiffness, sink and warp resistance. Modified for improved surface appearance.Data provided by the manufacturer |
|||
| Tensile Strength, Yield | 127 MPa | 18400 psi | SABIC - Japan Method |
| SABIC Innovative Plastics NORYL APS440 PPE+PPS (Asia Pacific) |
|||
| Tensile Strength, Yield | 127 MPa | 18500 psi | 5 mm/min; ASTM D638 |
| Samsung Cheil Industries Infino® VB-5300GS PBT, Glass Filled FR Information provided by Samsung Cheil Industries. |
|||
| Tensile Strength, Yield | 127 MPa @Thickness 3.20 mm |
18500 psi @Thickness 0.126 in |
5mm/min; ASTM D638 |
| LG Chemical LUMID LW4009A(W) PA6+GF/MF40%, Low Warpage Feature: Injection Molding, PA6+GF/MF40%, Low WarpageApplication: Automotive (Timing Belt Cover)CAS No. 25038-54-4, 13983-17-0 and 65997-17-3Information provided by LG Chemical |
|||