Huntsman IROGRAN® A 85 E 4993 FCM Polyester-Based TPU-Injection Extrusion Grade
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Polyester Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 85 E 4993 FCM Polyester-Based TPU-Injection Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
IROGRAN A 85 E 4993 FCM is a thermoplastic polyester polyurethane for melt calendaring. IROGRAN is part of the HUNTSMAN technical extrusion and injection molding product range and offers a specially designed, flexible material with a broad processing window. IROGRAN A 85 E 4993 FCM is a food contact materialPerformance Features: High wear resistance Good melt flow High elasticity Complies with FDA CFR 177.2600 Low colorApplications: Textile Coatings Technical molding Cable jacketingInformation provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D995 |
| Melt Index of Compound | 65 g/10 min @Load 10.0 kg, Temperature 190 °C |
65 g/10 min @Load 22.0 lb, Temperature 374 °F |
cm<sup>3</sup>/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 86 | 86 | ASTM D2240 |
| Hardness, Shore D | 36 | 36 | ASTM D2240 |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | DIN 53504 |
| Elongation at Break | 700 % | 700 % | ASTM D412 |
| 100% Modulus | 0.00590 GPa | 0.856 ksi | DIN 53504 |
| 300% Modulus | 0.0112 GPa | 1.62 ksi | DIN 53504 |
| Rebound | 35 % | 35 % | Bayshore; ASTM D2632 |
| Tear Strength | 103 kN/m | 590 pli | ASTM D624 |
| Abrasion | 25 | 25 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 25 % @Temperature 23.0 °C, Time 252000 sec |
25 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 50 % @Temperature 70.0 °C, Time 86400 sec |
50 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 145 - 160 °C | 293 - 320 °F | Huntsman/TMA |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not reported |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Extrusion |
| Front Barrel Temperature | 170 - 195 °C | 338 - 383 °F | Extrusion |
| Nozzle Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Adapter Temperature | 175 - 200 °C | 347 - 392 °F | Extrusion |
| Die Temperature | 175 - 205 °C | 347 - 401 °F | Extrusion |
| Roll Temperature | 160 - 180 °C | 320 - 356 °F | Front |
| 160 - 180 °C | 320 - 356 °F | Rear |
Users viewing this material also viewed the following:
- Precision Polymer Engineering P60B Polyacrylate Rubber
- DuPont™ Dartek® F-101 Nylon 6,6 Forming Film, 25 µm Thickness (discontinued **)
- Samsung Cheil Industries Infino® VB-5300GS PBT, Glass Filled FR
- SABIC Innovative Plastics LNP THERMOCOMP PF005 PA 6 (Europe-Africa-Middle East)
- Silberline Sparkle Silver Ultraâ„¢ 6605
- A. Schulman POLYBATCH™ White 8350/UV5 Concentrate Based In Polyethylene
- ExxonMobil EXACT™ 3139 Plastomer for Cast Film Applications
- Azoty Tarnow™ Tarnamid® T-27 MS Polyamide 6 - Natural
- Asahi Kasei Thermylene® P6-40FG-0684 40% Glass Fiber Reinforced, Heat and UV Stabilized
- Loctite® Nuva-Sil® 5091 High Adhesion Potting
Copyright © lookpolymers.com All Rights Reserved