Ravago Manufacturing Americas Hylon® N1043HL Nylon 6/6 (DAM)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylon® N1043HL Nylon 6/6 (DAM).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ASTM D792 |
| Water Absorption | 0.60 % | 0.60 % | 24 hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | 0.125 in; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 103 | 103 | ASTM D785 |
| Tensile Strength at Break | 221 MPa | 32000 psi | ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| Flexural Strength | 276 MPa | 40000 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm | 2.50 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 21.6 µm/m-°C @Temperature 20.0 °C |
12.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | 0.0590 in, BK |
| HB | HB | 0.118 in, BK |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 20.9 kV/mm | 530 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 282 - 304 °C | 540 - 580 °F | |
| Mold Temperature | 65.6 - 98.9 °C | 150 - 210 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.20 % | 0.20 % | |
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure | 750 to 1400 psi | |
| Injection Rate | Fast |
Users viewing this material also viewed the following:
- NOVA Chemicals Novapol® HF-Y450-A Hexene HDPE Film Resin
- Kinlead PM11 Metalizing Grade BOPP Plain Film (thickness: 15 µm)
- Sylvin Technologies 9925-75 Natural PVC Molding Compound
- Teknor Apex APEX® 3310-60 Polyvinyl Chloride, Flexible
- Master Bond EP21SC-1 Two Component Epoxy Resin System
- A. Schulman POLYBATCH™ Ivory 9035 Concentrate Based In Polyethylene
- DSM Akulon® Ultraflow™ K-FG6 Nylon 6-30% Glass Reinforced (European Grade) (Dry)
- ExxonMobil LLDPE LL 8446.21 Linear Low Density Polyethylene Resin (European Grade)
- Diamond Polymers ASA/PC 7030
- Dura-Bar 65-45-12 HRDS Continuously Cast Ductile Iron Bar Stock ASTM A536
Copyright © lookpolymers.com All Rights Reserved