Ravago Manufacturing Americas Hylon® N1000THLUV2 Polyamide 66 (discontinued **)

Category	Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Heat Stabilized
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ravago Manufacturing Americas Hylon® N1000THLUV2 Polyamide 66 (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Available in North America Additive: Heat Stabilizer, Lubricant and UV StabilizerFeatures: Lubricated, Heat Stabilized and Good ToughnessRoHS CompliantAuto Specifications: GM GMP.PA66.079 Color: BlackForm: Pellets Processing Method: Injection Molding Properties are for dry polymer unless noted.Information provided by Ravago.

Physical Properties	Metric	English	Comments
Specific Gravity	1.09 g/cc	1.09 g/cc	ASTM D792
Water Absorption	1.2 % @Time 86400 sec	1.2 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.013 - 0.017 cm/cm @Thickness 3.17 mm	0.013 - 0.017 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	94	94	Conditioned; ASTM D785
	114	114	ASTM D785
Tensile Strength, Yield	46.2 MPa	6700 psi	Conditioned; ASTM D638
	65.5 MPa	9500 psi	ASTM D638
Elongation at Break	40 %	40 %	ASTM D638
	130 %	130 %	Conditioned; ASTM D638
Flexural Strength	34.5 MPa	5000 psi	Conditioned; ASTM D790
	82.7 MPa	12000 psi	ASTM D790
Flexural Modulus	0.896 GPa	130 ksi	Conditioned; ASTM D790
	2.21 GPa	320 ksi	ASTM D790
Izod Impact, Notched	1.60 J/cm	3.00 ft-lb/in	ASTM D256
	2.14 J/cm	4.00 ft-lb/in	Conditioned; ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	113 µm/m-°C	63.0 µin/in-°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	229 °C	445 °F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	71.1 °C	160 °F	Unannealed; ASTM D648
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in
	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	Conditioned

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+13 ohm-cm	1.00e+13 ohm-cm	Conditioned; ASTM D257
	1.00e+15 ohm-cm	1.00e+15 ohm-cm	ASTM D257
Dielectric Constant	3.5	3.5	ASTM D150
	5.8	5.8	Conditioned; ASTM D150
Dielectric Strength	21.3 kV/mm	540 kV/in	Method A (Short-time); ASTM D149

Processing Properties	Metric	English	Comments
Melt Temperature	277 - 293 °C	530 - 560 °F
Mold Temperature	48.9 - 93.3 °C	120 - 200 °F
Drying Temperature	73.9 °C @Time 7200 - 14400 sec	165 °F @Time 2.00 - 4.00 hour
Moisture Content	<= 0.18 %	<= 0.18 %	Suggested Maximum
Back Pressure	0.138 - 0.414 MPa	20.0 - 60.0 psi
Screw Speed	40 - 120 rpm	40 - 120 rpm