Greene Tweed FLUORAZ® 797 Fluoroelastomer, FEPM
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Greene Tweed |
| Trade Name | FLUORAZ® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Greene Tweed FLUORAZ® 797 Fluoroelastomer, FEPM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Greene, Tweed`s Fluoraz® functions effortlessly in a variety of challenging process environments. Fluoraz performs well in aggressive chemicals where ultrapure materials are not required. Known for its capabilities in high-temperature environments and its chemical resistance, Greene, Tweed`s Fluoraz has proven field performance in both dynamic and static applications.Information provided by Greene Tweed.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D297 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 64 | 64 | After 70hrs @347°F in Stauffer 7700 |
| 80 | 80 | ASTM D2240 | |
| Hardness, Shore M | 83 | 83 | ASTM D2240 |
| Tensile Strength at Break | 14.5 MPa | 2100 psi | After 70hrs @347°F in Stauffer 7700 |
| 19.3 MPa | 2800 psi | ASTM D1414 | |
| Tensile Strength, Yield | 3.86 MPa | 560 psi | @50% Elongation; ASTM D1414 |
| 9.136 MPa | 1325 psi | @100% Elongation; ASTM D1414 | |
| Elongation at Break | 225 % | 225 % | ASTM D1414 |
| 258.75 % | 258.75 % | After 70hrs @347°F in Stauffer 7700 | |
| Coefficient of Friction | 0.50 | 0.50 | ASTM D1894 |
| Coefficient of Friction, Static | 0.80 | 0.80 | ASTM D1894 |
| Tear Strength Test | 315 | 315 | lb/in; ASTM D624 Die B |
| Compression Set | 27 % | 27 % | 22 hours @ 392°F @ 25% deflection; ASTM D395 |
| 40 % | 40 % | 22 hours @ 392°F @ 25% deflection; ASTM D395 | |
| 19 % @Temperature 23.0 °C |
19 % @Temperature 73.4 °F |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 232 °C | 450 °F | |
| Minimum Service Temperature, Air | -5.00 °C | 23.0 °F | |
| Shrinkage | 25.0 % @Temperature 175 °C, Time 252000 sec |
25.0 % @Temperature 347 °F, Time 70.0 hour |
in Stauffer 7700 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black |
Users viewing this material also viewed the following:
- Formosa Plastics Formolene® L62608A Film (Hexene Grade) LLDPE (discontinued **)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR N330 (HAF) Filler
- Saint-Gobain CHR® SG15-05(R) High Performance Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Unifrax Fiberfrax® Topcoat™ 2600 Insulating Mix
- DuPont™ Surlyn® 9910 Ionomer Resin, Zinc
- Arkema Group OREVAC® 18510P Grafted Maleic Anhydride Polyethylene
- Aptek UVIBOND 7100 Semi-rigid, UV-Curing Urethane Adhesive
- Aremco AREMCOLOX™ 502-676 Machinable Magnesium Oxide
Copyright © lookpolymers.com All Rights Reserved