Ravago Manufacturing Americas Hylon® N1000NL2 Nylon 6/6 (Cond)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylon® N1000NL2 Nylon 6/6 (Cond).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DAM; ASTM D792 |
| Water Absorption | 1.1 % | 1.1 % | 24 hrs, DAM; ASTM D570 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | 0.125 in, DAM; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 64 | 64 | ASTM D785 |
| Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
| Elongation at Break | 35 % | 35 % | ASTM D638 |
| Flexural Strength | 62.1 MPa | 9000 psi | ASTM D790 |
| Flexural Modulus | 1.65 GPa | 240 ksi | ASTM D790 |
| Izod Impact, Notched | 1.23 J/cm | 2.30 ft-lb/in | 73°F; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 7.0 @Frequency 100 Hz |
7.0 @Frequency 100 Hz |
ASTM D150 |
| Dielectric Strength | 21.5 kV/mm | 545 kV/in | ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 48.9 - 93.3 °C | 120 - 200 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | 0.20 % | 0.20 % | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Screw Speed | 40 - 140 rpm | 40 - 140 rpm |
Users viewing this material also viewed the following:
- Resin Technology Group 15 Metal Bonder Fusion™ Cyanoacrylate Instant Ethyl Adhesive
- DSM Akulon® Ultraflow™ K-FG0 Nylon 6-50% Glass Reinforced (European and Asian Grade) (Dry) (discontinued **)&
- Loxim 811 02T HB Polypropylene Compound, 10% Talc Filled, Flame Retardant
- Borealis Borecene Compact™ RM8406 Black Linear Polyethylene for Rotational Molding
- Clariant Renol PPOSP0001 Polyphenylene Oxide, Mineral Filled
- Fainplast Compounds Hax™ CAT 115/1 Catalyst for Cable Compound
- Bhansali Engineering Abstron KU602 ABS Heat Resistant
- SABIC Innovative Plastics ULTEM 1000 PEI
Copyright © lookpolymers.com All Rights Reserved