Ravago Manufacturing Americas Hylon® N1000L2 Nylon 6/6 (DAM)  (discontinued **)

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ravago Manufacturing Americas Hylon® N1000L2 Nylon 6/6 (DAM)  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Ravago
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ASTM D792
Water Absorption 1.3 %
1.3 %
24 hrs; ASTM D570
Linear Mold Shrinkage 0.015 cm/cm
0.015 in/in
0.125 in; ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell M 85
85
ASTM D785
Tensile Strength at Break 82.7 MPa
12000 psi
ASTM D638
Elongation at Break 30 %
30 %
ASTM D638
Flexural Strength 114 MPa
16500 psi
ASTM D790
Flexural Modulus 3.03 GPa
440 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm
1.00 ft-lb/in
73°F; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 82.8 µm/m-°C

@Temperature 20.0 °C
 46.0 µin/in-°F

@Temperature 68.0 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 238 °C
460 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 87.8 °C
190 °F
Unannealed; ASTM D648
Flammability, UL94 V-2
V-2
0.0591 in, BK
V-2
V-2
0.0591 in, NC
V-2
V-2
0.118 in, BK
V-2
V-2
0.118 in, NC
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Constant 3.7

@Frequency 100 Hz
 3.7

@Frequency 100 Hz
 ASTM D150
Dielectric Strength 22.6 kV/mm
575 kV/in
ASTM D149
Processing Properties Metric English Comments
Melt Temperature 271 - 293 °C
520 - 560 °F
Mold Temperature 48.9 - 93.3 °C
120 - 200 °F
Drying Temperature 73.9 °C
165 °F
Dry Time 2 - 4 hour
2 - 4 hour
Moisture Content 0.20 %
0.20 %
Back Pressure 0.345 - 0.689 MPa
50.0 - 100 psi
Screw Speed 40 - 140 rpm
40 - 140 rpm