- Ravago Manufacturing Americas Hylex® P1018LLT Polycarbonate
Ravago Manufacturing Americas Hylex® P1018LLT Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hylex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hylex® P1018LLT Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Ravago.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 18 g/10 min @Load 1.20 kg, Temperature 300 °C |
18 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 57.2 MPa | 8300 psi | ASTM D638 |
| Elongation at Break | 110 % | 110 % | ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm | 12.0 ft-lb/in | 0.125 in; ASTM D256 |
| 3.74 J/cm @Temperature -40.0 °C |
7.00 ft-lb/in @Temperature -40.0 °F |
0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | 143 °C | 290 °F | ASTM D1525 |
| Flammability, UL94 | V-2 | V-2 | 0.0620 in, NA |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 243 - 266 °C | 470 - 510 °F | |
| Middle Barrel Temperature | 254 - 271 °C | 490 - 520 °F | |
| Front Barrel Temperature | 271 - 282 °C | 520 - 540 °F | |
| Nozzle Temperature | 266 - 277 °C | 510 - 530 °F | |
| Melt Temperature | 271 - 288 °C | 520 - 550 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 3 - 12 hour | 3 - 12 hour | |
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Injection Pressure | 6.21 - 12.4 MPa | 900 - 1800 psi | |
| Back Pressure | 0.483 - 1.03 MPa | 70.0 - 150 psi | |
| Shot Size | 40 - 60 % | 40 - 60 % | |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure | 600 to 1100 psi |
Users viewing this material also viewed the following:
- Pearl Engineering PEPLPET FR-101-H Monofilament Resin
- Overview of materials for Polyphenylene Ether, PTFE Filled
- Solvay Chemicals NOCOLOK® Flux Plus Binder Mixture Potassium Fluoroaluminate
- SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66
- SABIC Innovative Plastics ULTEM HU1000 PEI (Asia Pacific)
- Solvay Specialty Polymers Hyflon® AD 40H Perfluoropolymer
- Master Bond EP34CA Low Viscosity Heat Resistant Epoxy System
- ExxonMobil Enmist EP 150
- DuPont Teijin Films Teijin® Tetoron® OX Polyester Film, 400 Gauge
- Beijing Chemical Industry KAIFA® MN-401 PA6 Resin
Copyright © lookpolymers.com All Rights Reserved