- A. Schulman SCHULAMID® 66 GF30H 30% Glass Fiber Reinforced, Heat Stabilized Nylon 66
A. Schulman SCHULAMID® 66 GF30H 30% Glass Fiber Reinforced, Heat Stabilized Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | A. Schulman, Inc. |
| Trade Name | SCHULAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman SCHULAMID® 66 GF30H 30% Glass Fiber Reinforced, Heat Stabilized Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.175 mm |
0.0030 in/in @Thickness 0.1250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 150 MPa | 21800 psi | ASTM D638 |
| Elongation at Break | 4.5 % | 4.5 % | ASTM D638 |
| Flexural Strength | 229.8 MPa | 33330 psi | ASTM D790 |
| Flexural Modulus | 9.763 GPa | 1416 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.47 J/cm | 14.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C | 490 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 461 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |
| Moisture Content | 0.080 - 0.12 % | 0.080 - 0.12 % |
Users viewing this material also viewed the following:
- Mytex Polymers AS171L-02US Polypropylene, 13% Talc Filled
- Oxford Polymers PC GR912-V0 UL Listed Polycarbonate
- PolyOne Edgetek® XT XT-100-BU03 Black Polycarbonate + PBT (PC+PBT)
- LG Chemical SEETEC H1501 Polypropylene Homopolymer
- Momentive Performance Materials Addisilâ„¢ 472 E Healthcare Extrusion Grade Heat Cured Rubber
- Dow Corning Q4-3667 Fluid
- EMS-Griltech Griltex® D 1516A Heat Stabilized Copolyamide Hotmelt Adhesive (Technical Applications)
- EMS-Grivory Grivory® EBGM-20 HX PA666-GF15
- Samyang Triel® 5722EM Thermoplastics Polyetherester Elastomer, Extrusion
- PolyOne Synprene® RT-4080 Thermoplastic Elastomer - SBC, Mineral Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved