SABIC Innovative Plastics LNP STAT-KON RE008 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON RE008 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-KON* RE008 is a compound based on Nylon 66 containing 40% Carbon Fiber. Characteristics of this grade include: Electrically Conductive.
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
ASTM D792
Mechanical Properties Metric English Comments
Tensile Strength at Break 259 MPa
37600 psi
Type I, 5 mm/min; ASTM D638
Tensile Modulus 33.33 GPa
4834 ksi
5 mm/min; ASTM D638
Flexural Strength 390 MPa
56600 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 25.0 GPa
3630 ksi
2 mm/min; ISO 178
25.58 GPa
3710 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.16 J/cm
2.17 ft-lb/in
ASTM D256
Izod Impact, Unnotched 10.69 J/cm
20.03 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
256 °C

@Thickness 3.20 mm
 493 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 10 - 10000 ohm
10 - 10000 ohm
ASTM D257