Ravago Manufacturing Americas Hybrid S470H Acrylonitrile Butadiene Styrene + PC Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Ravago Manufacturing Americas, LLC |
| Trade Name | Hybrid |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ravago Manufacturing Americas Hybrid S470H Acrylonitrile Butadiene Styrene + PC Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Available in North America Flame Retardant RoHS Compliant UL File Number: E157012 Form: Pellets Processing Method: Injection Molding Information provided by Ravago
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 8.5 g/10 min @Load 2.16 kg, Temperature 260 °C |
8.5 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 63.4 MPa | 9200 psi | ASTM D638 |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 6.41 J/cm @Thickness 3.17 mm |
12.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 124 °C | 255 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 249 - 260 °C | 480 - 500 °F | |
| Middle Barrel Temperature | 254 - 266 °C | 490 - 510 °F | |
| Front Barrel Temperature | 260 - 271 °C | 500 - 520 °F | |
| Nozzle Temperature | 260 - 277 °C | 500 - 530 °F | |
| Mold Temperature | 71.1 - 93.3 °C | 160 - 200 °F | |
| Drying Temperature | 104 - 110 °C @Time 7200 - 14400 sec |
220 - 230 °F @Time 2.00 - 4.00 hour |
|
| Dry Time | <= 10.0 hour | <= 10.0 hour | |
| Moisture Content | <= 0.040 % | <= 0.040 % | Suggested Maximum |
| Injection Pressure | 5.52 - 11.7 MPa | 800 - 1700 psi | |
| Back Pressure | 0.345 - 0.827 MPa | 50.0 - 120 psi | |
| Shot Size | 40 - 80 % | 40 - 80 % | |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Rate | Moderate |
Users viewing this material also viewed the following:
- Abatron 82122 A/B Filled Potting Compound (discontinued **)
- Global GAB-130 30% Glass Reinforced, General Purpose ABS
- LTL Color Compounds ColorRxâ„¢ PP2-1005ARX Biocompatible, Antimicrobial Polypropylene Random Copolymer
- Gwent Electronic Materials P2121112P2 Argon Plasma Modified Graphene Nanoplatelets
- LATI Larton K/30 PPS, 30% Carbon Fiber Reinforced
- A. Schulman POLYBATCH™ White 8350 EC1 Concentrate Based In LDPE
- ExxonMobil Exact™ 9071 Ethylene-based Plastomer Resin
- Epoxyset Epoxibond EB-103F Unfilled Epoxy Adhesive
- ConocoPhillips ANDEROL® FGH 32 Synthetic Food Grade Hydraulic Fluid, ISO 32
- AdvanSource Biomaterials ChronoFlex® AR Biodurable Medical Grade Polyurethane
Copyright © lookpolymers.com All Rights Reserved