Premix Thermoplastics PRE-ELEC® PP 1398 Conductive Thermoplastic Compound

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with Carbon Black Filler
Manufacturer	Premix Thermoplastics Inc.
Trade Name	PRE-ELEC®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Premix Thermoplastics PRE-ELEC® PP 1398 Conductive Thermoplastic Compound.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PRE-ELEC® PP 1398 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PP 1398 has an excellent balance of mechanical properties and is easy to injection mould.Applications: Include injection moulded crates, boxes, pallets and tote bins for electronic components and other static sensitive devides (SSD).Processing: PRE-ELEC® PP 1398 compound can be processed in the injection moulding machines using normal processing conditions as with polypropylene.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY

Physical Properties	Metric	English	Comments
Density	1.01 g/cc	0.0365 lb/in³
Thickness	102 microns	4.00 mil
Linear Mold Shrinkage	0.012 - 0.015 cm/cm	0.012 - 0.015 in/in	ISO 294-4
Melt Flow	1.0 g/10 min @Load 2.16 kg, Temperature 230 °C	1.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133
	10 g/10 min @Load 5.00 kg, Temperature 230 °C	10 g/10 min @Load 11.0 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	96	96	ISO 868
Hardness, Shore D	70	70	ISO 868
Tensile Strength	19.0 MPa	2760 psi	ISO 527
Tensile Strength, Yield	26.0 MPa	3770 psi	ISO 527
Elongation at Break	32 %	32 %	ISO 527
Elongation at Yield	12 %	12 %	ISO 527
Flexural Modulus	1.10 GPa	160 ksi	ISO 178
Izod Impact, Notched (ISO)	6.00 kJ/m² @Thickness 4.00 mm, Temperature -20.0 °C	2.86 ft-lb/in² @Thickness 0.157 in, Temperature -4.00 °F	ISO 180
	NB @Thickness 4.00 mm, Temperature 23.0 °C	NB @Thickness 0.157 in, Temperature 73.4 °F	ISO 180
Izod Impact, Unnotched (ISO)	24.0 kJ/m² @Thickness 4.00 mm, Temperature -20.0 °C	11.4 ft-lb/in² @Thickness 0.157 in, Temperature -4.00 °F	ISO 180
	NB @Thickness 4.00 mm, Temperature 23.0 °C	NB @Thickness 0.157 in, Temperature 73.4 °F	ISO 180
Charpy Impact Unnotched	NB @Thickness 102 mm, Temperature 23.0 °C	NB @Thickness 4.00 in, Temperature 73.4 °F	ISO 179
	NB @Thickness 102 mm, Temperature -20.0 °C	NB @Thickness 4.00 in, Temperature -4.00 °F	ISO 179
Charpy Impact, Notched	2.60 J/cm² @Thickness 102 mm, Temperature -20.0 °C	12.4 ft-lb/in² @Thickness 4.00 in, Temperature -4.00 °F	ISO 179
	3.00 J/cm² @Thickness 102 mm, Temperature 23.0 °C	14.3 ft-lb/in² @Thickness 4.00 in, Temperature 73.4 °F	ISO 179

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	74.0 °C	165 °F	75/Method Bf
Deflection Temperature at 1.8 MPa (264 psi)	46.0 °C	115 °F	75/Method Af
Vicat Softening Point	90.0 °C	194 °F	ISO 306/B50
	143 °C	289 °F	ISO 306/A50

Electrical Properties	Metric	English	Comments
Volume Resistivity	<= 1000 ohm-cm	<= 1000 ohm-cm	ISO D-257
Surface Resistance	<= 10000 ohm	<= 10000 ohm	ISO IEC 61340-5-1

Processing Properties	Metric	English	Comments
Melt Temperature	200 - 260 °C	392 - 500 °F
Mold Temperature	60.0 - 80.0 °C	140 - 176 °F
Drying Temperature	60.0 - 80.0 °C	140 - 176 °F	Pre-drying
Dry Time	2 - 4 hour	2 - 4 hour
Injection Pressure	60.0 - 80.0 MPa	8700 - 11600 psi
Shelf Life	12.0 Month	12.0 Month	Normal Storing Conditions

Descriptive Properties	Value	Comments
Injection Speed	Moderate