Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage | 0.012 - 0.015 cm/cm | 0.012 - 0.015 in/in | With Flow; ISO 2577 |
Polykemi AB POLYelast TPE EC90 D50 P05B Thermoplastic Elastomer, PP/EPDM Information provided by Polykemi AB |
|||
Linear Mold Shrinkage | 0.010 - 0.015 cm/cm | 0.010 - 0.015 in/in | |
Qualchem Danamid AFCF-30 Polyamide 66, 30% Carbon Fiber Reinforced with carbon fiber, antistatic and conductive.Information provided by Qualchem Zrt. |
|||
Linear Mold Shrinkage | 0.010 - 0.015 cm/cm | 0.010 - 0.015 in/in | FRISETTA Test Method |
Nilit FRIANYL A63 CV30 Nylon 6.6 for injection molding, 30% carbon fiber reinforced Nylon 6.6 for injection molding (good conductive and electrostatic properties).Information provided by Frisetta Polymer, which merged into Nilit Plastics |
|||
Linear Mold Shrinkage | 0.010 - 0.015 cm/cm | 0.010 - 0.015 in/in | ASTM D955 |
PolyOne Lubri-Tech™ AT-15GP/5T Acetal-Copolymer, PTFE Lubricated
(discontinued **) Description/Features:Graphite LubricatedPTFE LubricatedInformation provided by PolyOne Corporation. |
|||
Linear Mold Shrinkage | 0.0090 - 0.015 cm/cm | 0.0090 - 0.015 in/in | |
Lehmann & Voss LUVOCOM® 1105-8174 PEEK, with PTFE, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Chemical and hydrolysis resistance parts, non flammable.Improved friction and wear behavio.. |
|||
Linear Mold Shrinkage | 0.010 - 0.015 cm/cm | 0.010 - 0.015 in/in | |
Lehmann & Voss LUVOCOM® 19-7652 Polyamide 46, with PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Reduced moment of inertia comp.. |
|||
Linear Mold Shrinkage | 0.011 - 0.015 cm/cm | 0.011 - 0.015 in/in | |
Lehmann & Voss LUVOCOM® 3-8266 Polyamide 6, unreinforced Applications: Automotive industry, textile machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.Isotropic shrinkage characteristics.Reduce.. |
|||
Linear Mold Shrinkage | 0.010 - 0.015 cm/cm | 0.010 - 0.015 in/in | |
Lehmann & Voss LUVOCOM® 6-8503/BL Polyamide 12, unreinforced Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Dynamic stressed parts.Low waterabsorbtion.Isotropic shrinkage characteristics.Bearings, sleeve.. |
|||
Linear Mold Shrinkage | 0.013 - 0.015 cm/cm | 0.013 - 0.015 in/in | ASTM D955 |
Kolon KOPA® KN131 General Purpose Nylon 6 KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in automobile and industrial parts.Good mechanical properties, outstanding self-lubr.. |
|||
Linear Mold Shrinkage | 0.013 - 0.015 cm/cm | 0.013 - 0.015 in/in | ASTM D1299 |
Loxim 820 02T HB Polypropylene Compound, 20% Talc Filled, Flame Retardant Information provided by Loxim Industries |
|||
Linear Mold Shrinkage | 0.010 - 0.015 cm/cm | 0.010 - 0.015 in/in | |
Lehmann & Voss LUVOCOM® GS-H/2 Polyamide 66, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Emergency running property.Isotropic shrinkage characteristics.Control disks, cams, sliding ele.. |
|||
Linear Mold Shrinkage | 0.010 - 0.015 cm/cm | 0.010 - 0.015 in/in | ASTM D955 |
Teknor Apex Chemlon® 223 Nylon 6, Unreinforced Features: Nucleated for fast cyclingProcessing Method: Injection MoldingForms: Pellets Additive: Nucleating AgentInformation Provided by Teknor Apex |
|||
Linear Mold Shrinkage | 0.011 - 0.015 cm/cm @Thickness 3.20 mm |
0.011 - 0.015 in/in @Thickness 0.126 in |
72 hr; ISO 294 |
A. Schulman FORMION™ FI 391 Ionomer DescriptionFormion® FI 391 is a non-reinforced, injection molding grade Ionomer, which has been formulated for scratch resistance, low temperature ductility, and medium stiffness. Formion F1 391U i.. |
|||
Linear Mold Shrinkage | 0.0050 - 0.015 cm/cm @Thickness 3.175 mm |
0.0050 - 0.015 in/in @Thickness 0.1250 in |
ASTM D955 |
A. Schulman SCHULAMID® 66 MK20HI 20% Mineral Reinforced, Impact Modified Nylon 66 Information provided by A. Schulman. |
|||
Linear Mold Shrinkage | 0.0080 - 0.015 cm/cm | 0.0080 - 0.015 in/in | ASTM D955 |
Cheng Yu Plastic N6CV1 Flame Retardant Nylon 6, 10% Mineral Reinforced |
|||
Linear Mold Shrinkage | 0.0080 - 0.015 cm/cm | 0.0080 - 0.015 in/in | ASTM D955 |
Cheng Yu Plastic NGCV2 Flame Retardant Nylon 6, 20% Mineral Reinforced |
|||
Linear Mold Shrinkage | 0.0020 - 0.015 cm/cm | 0.0020 - 0.015 in/in | ASTM D955 |
Cheng Yu Plastic T890G3 PBT, 30% Glass Fiber |
|||
Linear Mold Shrinkage | 0.012 - 0.015 cm/cm | 0.012 - 0.015 in/in | ASTM D 955 |
Cossa Polimeri ESTAPROP KUR 1010 TG05 Polypropylene, 5% Mineral Filled PP copolymer 5% mineral fillerElastomer modified, very high impact strength at low temperatureInformation provided by Cossa Polimeri S.r.l. |
|||
Linear Mold Shrinkage | 0.0050 - 0.015 cm/cm | 0.0050 - 0.015 in/in | ASTM D955 |
Cheng Yu Plastic FV30715 POM, 15% Mineral Reinforced |