Polyram RamTal PM1429 Polyacetal, PTFE Filled
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, PTFE Filled |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTal PM1429 Polyacetal, PTFE Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyacetal filled with PTFE for sliding parts, low friction and improved wear resistance of molded parts.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 - 1.50 g/cc | 0.0524 - 0.0542 lb/in³ | ISO 1183 |
| Water Absorption at Saturation | 0.22 % | 0.22 % | ISO 62 |
| Linear Mold Shrinkage | 0.018 - 0.022 cm/cm | 0.018 - 0.022 in/in | ISO 2577 |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Break | 35 % | 35 % | ISO 527 |
| Tensile Modulus | 2.00 GPa | 290 ksi | ISO 527 |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Flexural Modulus | 1.90 GPa | 276 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 155 °C | 311 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
Users viewing this material also viewed the following:
- ExxonMobil Escorene® LD-401 EVA for Electrical Insulation (discontinued **)
- Albis Plastics Cellulose Acetate Propionate CP800 (Base Grade), 10% Plasticizer (discontinued **)
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR Hi-Sil 243 LD Filler
- Westlake Plastics Zelux® 10% GF Polycarbonate 10% Glass Filled
- Tra-Con Tra-Bond F156 Optically Opaque Epoxy Adhesive
- A. Schulman POLYBATCH™ Ivory 9035 Concentrate Based In Polyethylene
- BASF Ultradur B 4040 G10 BK5110 50% Glass Filled PBT
- Guarniflon PTFE G300 Polytetrafluoroethylene
- ChevronTexaco Bright-Cut® AD Metal Working Fluid
Copyright © lookpolymers.com All Rights Reserved