BASF Ultramid® B3UGM210 GR 22866 10/50% Glass/Mineral Filled PA6 FR (Conditioned)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass/Mineral Reinforced |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® B3UGM210 GR 22866 10/50% Glass/Mineral Filled PA6 FR (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Halogen- and phosphorus-free injection-molding grade with very high rigidity, low smoke density and outstanding electrical properties.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in³ | ISO 1183 |
| Water Absorption | 4.1 - 4.7 % | 4.1 - 4.7 % | Saturation; ISO 62 |
| Moisture Absorption at Equilibrium | 1.0 - 1.4 % | 1.0 - 1.4 % | 23°C; 50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | restricted |
| Melt Flow | 41.75 g/10 min @Load 5.00 kg, Temperature 275 °C |
41.75 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | 50 mm/min; ISO 527-1/-2 |
| Elongation at Yield | 2.5 % | 2.5 % | 50 mm/min; ISO 527-1/-2 |
| Modulus of Elasticity | 6.50 GPa | 943 ksi | ISO 527-1/-2 |
| Flexural Strength | 115 MPa | 16700 psi | at max force; ISO 178 |
| Charpy Impact Unnotched | 3.00 J/cm² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 0.270 J/cm² @Temperature 23.0 °C |
1.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.40 J/g-°C | 0.335 BTU/lb-°F | |
| Thermal Conductivity | 1.00 W/m-K | 6.94 BTU-in/hr-ft²-°F | DIN 52612 |
| Melting Point | 220 °C | 428 °F | DIN 53765 |
| Maximum Service Temperature, Air | 149 °C | 300 °F | for 50% loss of tensile strength after 20000hr |
| 167 °C | 333 °F | for 50% loss of tensile strength after 5000hr | |
| 200 °C | 392 °F | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 5.0 @Frequency 1.00 Hz |
5.0 @Frequency 1.00 Hz |
IEC 60250 |
| Dissipation Factor | 0.050 @Frequency 1.00e+6 Hz |
0.050 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | Injection-molding/Extrusion |
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | GR 22866 | |
| Commercial Status | Europe |
Users viewing this material also viewed the following:
- Pyrotek V-5 Fiberglass Fabric
- SCG Chemicals EL-Leneâ„¢ M3504DXP Octene (C8) Rotational Molding Resin
- ExxonMobil Exceed™ 1327KD Metallocene Polyethylene Resin (European Grade)
- DuPont Performance Polymers VTR GLT Peroxide Cured Fluoroelastomer (FKM) Formulation
- Aclo Accutech Polyethylene HD0204UVL High Density UV Stabilized
- Asia International Enterprise (Hong Kong) 6010FGN Nylon 66
- BLUESTAR 201-G25202 PBT, 25% Glass Filled
- Asahi Kasei Xyron® AT610 Modified Polyphenylene Ether
- Lubrizol ESTANE® 54620 Ester Based Thermoplastic Polyurethane (European Grade)
Copyright © lookpolymers.com All Rights Reserved