PolyOne Therma-Tech™ SF-4500 TC Polyphenylene Sulfide (PPS)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Therma-Tech™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Therma-Tech™ SF-4500 TC Polyphenylene Sulfide (PPS).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.67 g/cc | 1.67 g/cc | ASTM D792 |
| Water Absorption | 0.040 % | 0.040 % | @ 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 123 | 123 | ASTM D785 |
| Tensile Strength at Break | 100 MPa | 14500 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 31.0 GPa | 4500 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 296 MPa | 42900 psi | ASTM D790 |
| Flexural Modulus | 20.0 GPa | 2900 ksi | ASTM D790 |
| Compressive Strength | 193 MPa | 28000 psi | ASTM D695 |
| Izod Impact, Notched | 0.170 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.318 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 11.0 µm/m-°C | 6.11 µin/in-°F | ASTM D696 |
| Thermal Conductivity | 11.0 W/m-K | 76.3 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 299 °C @Thickness 3.18 mm |
570 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 263 °C @Thickness 3.18 mm |
505 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 80 - 100 ohm-cm | 80 - 100 ohm-cm | ASTM D257 |
| Surface Resistance | 80 - 100 ohm | 80 - 100 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 304 - 332 °C | 579 - 630 °F | |
| Mold Temperature | 121 - 149 °C | 250 - 300 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| Dry Time | 6.00 hour | 6.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Electrically Conductive | |
| Thermally Conductive | ||
| Forms | Pellets | |
| Generic Material | PPS | |
| Generic Name | Polyphenylene Sulfide (PPS) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |
Users viewing this material also viewed the following:
- Nye Lubricants 723K (RL) Rheolube Grease
- Polykemi AB POLYfill PPH K20020 D Polypropylene Homopolymer, Mineral Reinforced, Detergent Resistant
- PolyOne Therma-Tech™ NJ-6000C TC Nylon 12 (discontinued **)
- Solvay ALKAMULS® A 9 Surfactant
- Polyram PlusTek RA303G50 Nylon 66 for Injection Molding, 50% Glass Fiber Reinforced, Heat Stabilized, Hydrolysis Resistant
- CP-Polymer-Technik Wellamid® 6600/58 GV 30 HWCP 30% Glass Fiber Nylon 66, Impact Modified Until -40°C, Heat Stabilized, Dry
- Arlon 30580R020 0.020" (0.508 mm) Uncured Unsupported Silicone Rubber on Kodacel Carrier
- 3M 7248 Graffiti Resistant Overlaminating Label Product
- Quadrant EPP Duratron® U2100 OEI Extruded 10% Glass Reinforced Polyetherimide
Copyright © lookpolymers.com All Rights Reserved