Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

LG Chemical 90HR SAN, High Transparency, Heat Resistance, Chemical Resistance

Category Polymer , Thermoplastic , SAN Polymer
Manufacturer LG Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF LG Chemical 90HR SAN, High Transparency, Heat Resistance, Chemical Resistance.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Feature: Injection Molding, SAN, High Transparency, Heat Resistance, Chemical ResistanceApplication: Battery Case, Light CoverCAS No. 9003-54-7Information provided by LG Chemical
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D792
Maximum Moisture Content 0.010
0.010
Injection Molding
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0040 - 0.0070 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 2.0 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 2.0 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 ASTM D1238
10 g/10 min

@Load 3.80 kg,
Temperature 230 °C
 10 g/10 min

@Load 8.38 lb,
Temperature 446 °F
 ASTM D1238
27 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 27 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 124
124
ASTM D785
Tensile Strength, Yield 76.5 MPa

@Thickness 3.20 mm
 11100 psi

@Thickness 0.126 in
 50mm/min; ASTM D638
Elongation at Break 9.0 %

@Thickness 3.20 mm
 9.0 %

@Thickness 0.126 in
 50mm/min; ASTM D638
Tensile Modulus 3.21 GPa

@Thickness 3.20 mm
 465 ksi

@Thickness 0.126 in
 1 mm/min; ASTM D638
Flexural Yield Strength 125 MPa

@Thickness 3.20 mm
 18100 psi

@Thickness 0.126 in
 15mm/min; ASTM D790
Flexural Modulus 3.77 GPa

@Thickness 3.20 mm
 546 ksi

@Thickness 0.126 in
 15mm/min; ASTM D790
Izod Impact, Notched 0.0981 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
 0.184 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
 ASTM D256
0.0981 J/cm

@Thickness 6.40 mm,
Temperature -30.0 °C
 0.184 ft-lb/in

@Thickness 0.252 in,
Temperature -22.0 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) >= 92.0 °C

@Thickness 6.40 mm
 >= 198 °F

@Thickness 0.252 in
 Unannealed; ASTM D648
Vicat Softening Point 103 °C

@Load 5.00 kg
 217 °F

@Load 11.0 lb
 50°C/h; ASTM D1525
UL RTI, Electrical 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
 122 °F

@Thickness >=0.118 in
UL RTI, Mechanical with Impact 50.0 °C

@Thickness >=1.50 mm
 122 °F

@Thickness >=0.0591 in
50.0 °C

@Thickness >=3.00 mm
 122 °F

@Thickness >=0.118 in
UL RTI, Mechanical without Impact 50.0 °C

@Thickness <=1.50 mm
 122 °F

@Thickness <=0.0591 in
50.0 °C

@Thickness <=3.00 mm
 122 °F

@Thickness <=0.118 in
Flammability, UL94 HB

@Thickness >=1.60 mm
 HB

@Thickness >=0.0630 in
HB

@Thickness >=3.20 mm
 HB

@Thickness >=0.126 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
Dielectric Strength 27.0 kV/mm
686 kV/in
Arc Resistance 120 - 180 sec
120 - 180 sec
ASTM D495
Comparative Tracking Index 400 - 600 V
400 - 600 V
Hot Wire Ignition, HWI 7.0 - 15 sec

@Thickness >=1.50 mm
 7.0 - 15 sec

@Thickness >=0.0591 in
15 - 30 sec

@Thickness >=3.00 mm
 15 - 30 sec

@Thickness >=0.118 in
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 1.50 mm
 >= 120 arcs

@Thickness 0.0591 in
>= 120 arcs

@Thickness 3.00 mm
 >= 120 arcs

@Thickness 0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 170 - 190 °C
338 - 374 °F
Injection Molding
Middle Barrel Temperature 180 - 200 °C
356 - 392 °F
Injection Molding
Front Barrel Temperature 190 - 210 °C
374 - 410 °F
Injection Molding
Nozzle Temperature 190 - 220 °C
374 - 428 °F
Injection Molding
Melt Temperature 190 - 220 °C
374 - 428 °F
Injection Molding
Mold Temperature 40.0 - 70.0 °C
104 - 158 °F
Injection Molding
Drying Temperature 80.0 °C
176 °F
Injection Molding
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Injection Molding
Back Pressure 29.4 - 58.8 MPa
4260 - 8530 psi
Injection Molding
Screw Speed 30 - 60 rpm
30 - 60 rpm
Injection Molding