- Polyram PlusTek RA102 Nylon 6.6, General Purpose
Polyram PlusTek RA102 Nylon 6.6, General Purpose
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek RA102 Nylon 6.6, General Purpose.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DIN 53479 |
| Water Absorption | 1.0 % | 1.0 % | DIN 53495 |
| Linear Mold Shrinkage | 0.015 - 0.018 cm/cm | 0.015 - 0.018 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | >= 115 | >= 115 | ASTM-D785 |
| Tensile Strength, Yield | >= 75.0 MPa | >= 10900 psi | ASTM-D638 |
| Elongation at Break | >= 15 % | >= 15 % | ASTM-D638 |
| Flexural Strength | >= 100 MPa | >= 14500 psi | ASTM D790 |
| Flexural Modulus | >= 2.40 GPa | >= 348 ksi | ASTM-D790 |
| Izod Impact, Notched | >= 0.550 J/cm @Temperature 23.0 °C |
>= 1.03 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous Use |
| 200 °C | 392 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 190 °C | >= 374 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 80.0 °C | >= 176 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | DIN 53482 |
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz |
3.6 @Frequency 1e+6 Hz |
VDE 0303/4 |
| Dielectric Strength | 120 kV/mm | 3050 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- NEXA® PFX8010 Perfluoroelastomer
- Palm Labs Adhesives Turbo Fuse Series 160SI Surface Insensitive (1000 Viscosity) Rapid Bonding Adhesive
- Johnson Matthey Argo-braze 49H Silver Brazing Alloy for Tungsten Carbide Brazing
- Momentive Performance Materials HCT-S Titanium Diboride (TiB2) Powder
- Lanxess Durethan® BC 550 Z DUSXBL 900116 Nylon 6, Impact Modified
- Techmer ES Elastoblend® PA6 GF30 IM L 30% Glass Filled
- UBE UBEPOL VCR412 Synthetic Rubber Vulcanizate (Cured 50 Minutes at 145°C)
- 3M FP026508 White Polyester Label Products
- DuPont Performance Polymers Zytel® 74G33W BK196 Nylon 66 (Unverified Data**)
- Bhansali Engineering Abstron MIF-45 ABS Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved