Materion Beryllium Copper Alloy 25 Strip; AT (TF00) Temper (UNS C17200)
| Category | Metal , Nonferrous Metal , Beryllium Alloy , Copper Alloy |
| Manufacturer | Materion Corporation (former Brush Wellman) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Materion Beryllium Copper Alloy 25 Strip; AT (TF00) Temper (UNS C17200).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Treatment required for max strength: 3 hrs @ 315ºCStress Relaxation-% Stress Remaining after 1000 hrs @ 100°C: 96%Stress Relaxation after 1000 hrs @ 200°C: 70%Superficial Hardness: 30N 56-62Tabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.36 g/cc | 0.302 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell C | 36 - 42 | 36 - 42 | |
| Hardness, Vickers | 353 - 413 | 353 - 413 | |
| Tensile Strength, Ultimate | 1130 - 1350 MPa | 164000 - 196000 psi | |
| Tensile Strength, Yield | 960 - 1210 MPa | 139000 - 175000 psi | |
| Elongation at Break | 3.0 - 15 % | 3.0 - 15 % | |
| Modulus of Elasticity | 131 GPa | 19000 ksi | |
| Fatigue Strength | 280 - 310 MPa @# of Cycles 1.00e+8 |
40600 - 45000 psi @# of Cycles 1.00e+8 |
Reverse Bending (R=1) |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 17.0 µm/m-°C @Temperature 20.0 - 200 °C |
9.44 µin/in-°F @Temperature 68.0 - 392 °F |
|
| Thermal Conductivity | 105 W/m-K | 729 BTU-in/hr-ft²-°F | |
| Melting Point | 870 - 980 °C | 1600 - 1800 °F | |
| Solidus | 870 °C | 1600 °F | |
| Liquidus | 980 °C | 1800 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Beryllium, Be | 1.8 - 2.0 % | 1.8 - 2.0 % | |
| Co + Ni | >= 0.20 % | >= 0.20 % | |
| Co + Ni + Fe | <= 0.60 % | <= 0.60 % | |
| Copper, Cu | 98 % | 98 % | as balance |
| Lead, Pb | <= 0.020 % | <= 0.020 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.00000610 - 0.00000780 ohm-cm | 0.00000610 - 0.00000780 ohm-cm | 22-28% IACS Conductivity |
Users viewing this material also viewed the following:
- MV Labs YB400 YbCl3·6H2O Ytterbium chloride hexahydrate
- SABIC Innovative Plastics Lexan® EXL9112 PC Copolymer (Europe-Africa-Middle East)
- Hong Kun Group DBDPE Flame Retardant
- Fine Organics FINALUX G 401 Lubricant Additive
- Lanxess Durethan® T 40 ZS 000000 Partially aromatic polyamide
- SABIC Innovative Plastics ULTEM DT1810EV PEI Blend (Asia Pacific)
- Silikony Polskie Polsil E5S Silicone Emulsion
- DuPont™ Surlyn® 8528 Sodium Ionomer
Copyright © lookpolymers.com All Rights Reserved