Polymer Resources PC/TP-GP2 PC Polyester, High Impact, Excellent Chemical Resistance (Unverified Data**)&

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources PC/TP-GP2 PC Polyester, High Impact, Excellent Chemical Resistance (Unverified Data**)&.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Density	1.22 g/cc	0.0441 lb/in³	ASTM D792
Linear Mold Shrinkage	0.0060 - 0.0090 cm/cm	0.0060 - 0.0090 in/in	ASTM D955
Melt Flow	5.0 - 15 g/10 min	5.0 - 15 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	51.7 MPa	7500 psi	ASTM D638
Tensile Strength, Yield	50.3 MPa	7300 psi	ASTM D638
Flexural Strength	74.5 MPa	10800 psi	ASTM D790
Flexural Modulus	2.07 GPa	300 ksi	ASTM D790
Izod Impact, Notched	8.54 J/cm	16.0 ft-lb/in	ASTM D256
	4.27 J/cm @Temperature -40.0 °C	8.00 ft-lb/in @Temperature -40.0 °F	ASTM D256
Gardner Impact	>= 36.2 J	>= 26.7 ft-lb	ASTM D3029

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	93.3 °C	200 °F	ASTM D648
Flammability, UL94	HB	HB	1/16 in
	HB	HB	1/8 in

Processing Properties	Metric	English
Rear Barrel Temperature	249 - 271 °C	480 - 520 °F
Middle Barrel Temperature	254 - 277 °C	490 - 530 °F
Front Barrel Temperature	260 - 282 °C	500 - 540 °F
Melt Temperature	246 - 274 °C	475 - 525 °F
Mold Temperature	65.6 - 87.8 °C	150 - 190 °F
Drying Temperature	104 - 110 °C	220 - 230 °F
Dry Time	4 - 6 hour	4 - 6 hour