Polymer Resources PC/TP-FR3 Flame Retardant PC/Polyester Alloy
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP |
| Manufacturer | Polymer Resources, LTD |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polymer Resources PC/TP-FR3 Flame Retardant PC/Polyester Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame Retardant, High Impact, Excellent Chemical ResistanceFeatures: • Flame Retardant • Impact Modified • Self Extinguishing • Good Chemical ResistanceProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.011 - 0.013 cm/cm | 0.011 - 0.013 in/in | ASTM D955 |
| Melt Flow | 12 - 20 g/10 min @Load 2.16 kg, Temperature 265 °C |
12 - 20 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 49.0 MPa | 7100 psi | ASTM D638 |
| Tensile Strength, Yield | 42.7 MPa | 6200 psi | ASTM D638 |
| Flexural Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 5.87 J/cm @Temperature 22.8 °C |
11.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Gardner Impact | 36.2 J | 26.7 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 98.9 °C | 210 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.2 °C | 180 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.59 mm |
V-0 @Thickness 0.0626 in |
|
| V-0 @Thickness 3.17 mm |
V-0 @Thickness 0.125 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 249 - 271 °C | 480 - 520 °F | |
| Middle Barrel Temperature | 249 - 282 °C | 480 - 540 °F | |
| Front Barrel Temperature | 249 - 282 °C | 480 - 540 °F | |
| Melt Temperature | 246 - 274 °C | 475 - 525 °F | |
| Mold Temperature | 65.6 - 87.8 °C | 150 - 190 °F | |
| Drying Temperature | 110 - 116 °C | 230 - 240 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Vent | 0.0015 |
Users viewing this material also viewed the following:
- MV Labs RU470 {Ru(NH3)6}Cl2 Hexamineruthenium(II) chloride
- Polimeri Europa Europrene® N 3380 Acrylonitrile-Butadiene Rubber
- PTS Tristar® PC-10GFR-(V) 10% Glass Reinforced UV Stabilized Polycarbonate With Release
- Lehmann & Voss LUVOCOM® 50-1375 Polycarbonate, with carbon fiber, glass fiber and PTFE
- Lucas-Milhaupt EASY FLO 3 Carbide Brazing Alloy
- Techmer ES Plastiblend® PC/PET IM 1016 UV
- Teknor Apex Monprene® MP-2375A Thermoplastic Elastomer
- Borealis BorPURE™ RB501BF Polypropylene Copolymer
- Duratherm FG Paraffinic Heat Transfer Fluid
Copyright © lookpolymers.com All Rights Reserved