Kolon KOPA® KN3322VO Flame Retardant Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN3322VO Flame Retardant Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
KOPA® is a thermoplastic resin with excellent mechanical, thermal and electrical properties and is widely used in the automobile, electrical and industrial parts.High tensile strength, outstanding self lubrication and abrasion resistance, excellent chemical & weather resistance, high usage temperatureInformation provided by US distributor, API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | DIN 53479; ASTM D792 |
| Water Absorption | 0.60 % | 0.60 % | DIN 53475; ASTM D570 |
| Linear Mold Shrinkage | 0.013 - 0.016 cm/cm | 0.013 - 0.016 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | DIN 53505; ASTM D785 |
| Tensile Strength, Ultimate | 80.4 MPa | 11700 psi | DIN 53455; ASTM D638 |
| Elongation at Break | 15 % | 15 % | DIN 53455; ASTM D638 |
| Flexural Yield Strength | 132 MPa | 19200 psi | DIN 53455; ASTM D790 |
| Flexural Modulus | 3.14 GPa | 455 ksi | DIN 53452; ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | DIN 53453; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
DIN 53752; ASTM D696 |
| Melting Point | 255 °C | 491 °F | DIN 53736; ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | DIN 53461; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | DIN 53461; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.4 @Frequency 1e+6 Hz |
3.4 @Frequency 1e+6 Hz |
ASTM D150/DIN 53483 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149/DIN 53481 |
| Arc Resistance | 125 sec | 125 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Overview of materials for Polytetrafluoroethylene (PTFE), Molded
- Styrolution Luran® S 776 SE ASA
- SK Chemicals SKYTHANE® X595A Polyester Based Thermoplastic Polyurethane Elastomer
- Teknor Apex APEX® 1001 Polyvinyl Chloride, Flexible
- Eurofoam Siliconcell 411/PLT Platinic Silicone Foam
- California Fine Wire Alloy 422 Precious Metal Alloy
- California Fine Wire Alloy 446 Precious Metal Alloy
- 3M 7800 Aluminum Foil Label Material
- Heraeus Clevios™ S V4 Antistatic/Conductive Polymer Coating for Screen Printing
Copyright © lookpolymers.com All Rights Reserved