Polymer Resources PC-FR-IM1 Polycarbonate, Preliminary Data Sheet, Low Temperature Impact and Flame Retardant

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Unreinforced, Flame Retardant
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PC-FR-IM1 Polycarbonate, Preliminary Data Sheet, Low Temperature Impact and Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Molding or ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 5.0 - 10 g/10 min
5.0 - 10 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.8 MPa
7800 psi
ASTM D638
Tensile Strength, Yield 53.8 MPa
7800 psi
ASTM D638
Flexural Strength 75.8 MPa
11000 psi
ASTM D790
Flexural Modulus 2.00 GPa
290 ksi
ASTM D790
Izod Impact, Notched 7.47 J/cm
14.0 ft-lb/in
ASTM D256
6.41 J/cm

@Temperature -40.0 °C
12.0 ft-lb/in

@Temperature -40.0 °F
ASTM D256
Gardner Impact >= 36.2 J
>= 26.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 129 °C
265 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 124 °C
255 °F
ASTM D648
Flammability, UL94 V-1
V-1
1/8 in
Processing Properties Metric English Comments
Rear Barrel Temperature 271 - 293 °C
520 - 560 °F
Middle Barrel Temperature 282 - 304 °C
540 - 580 °F
Front Barrel Temperature 293 - 316 °C
560 - 600 °F
Melt Temperature 282 - 316 °C
540 - 600 °F
Mold Temperature 71.1 - 93.3 °C
160 - 200 °F
Drying Temperature 118 - 124 °C
245 - 255 °F
Dry Time 3 - 4 hour
3 - 4 hour