Polykemi AB POLYfill PPC TS20020 UV Polypropylene Copolymer, Mineral Reinforced, UV-Stabilized

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene with 20% Talc Filler
Manufacturer Polykemi AB
Trade Name POLYfill
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYfill PPC TS20020 UV Polypropylene Copolymer, Mineral Reinforced, UV-Stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ISO 1183
Filler Content 20 %
20 %
±2%; Polykemi
Linear Mold Shrinkage 0.010 - 0.012 cm/cm
0.010 - 0.012 in/in
With Flow; ISO 2577
0.010 - 0.012 cm/cm
0.010 - 0.012 in/in
Across Flow; ISO 2577
Melt Index of Compound 20 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 20 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 30.0 MPa
<= 4350 psi
ISO/R527
Elongation at Break 30 %
30 %
ISO/R527
Elongation at Yield 6.0 %
6.0 %
ISO/R527
Flexural Strength <= 50.0 MPa
<= 7250 psi
ISO 178
Flexural Modulus 2.00 GPa

@Temperature 23.0 °C
 290 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179
NB

@Temperature -20.0 °C
 NB

@Temperature -4.00 °F
 ISO 179
Charpy Impact, Notched 0.200 J/cm²

@Temperature -20.0 °C
 0.952 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
0.500 J/cm²

@Temperature 23.0 °C
 2.38 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
CTE, linear 70.0 - 90.0 µm/m-°C
38.9 - 50.0 µin/in-°F
Polykemi
Deflection Temperature at 0.46 MPa (66 psi) 112 °C
234 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 67.0 °C
153 °F
120°C/h; ISO 75/1
Vicat Softening Point 75.0 °C

@Load 5.001 kg
 167 °F

@Load 11.03 lb
 50°C/h; ISO 306
145 °C

@Load 1.00 kg
 293 °F

@Load 2.21 lb
 50°C/h; ISO 306
Processing Properties Metric English Comments
Melt Temperature 205 - 260 °C
401 - 500 °F
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Dry Time 2 - 4 hour
2 - 4 hour
in circulation dryer
2 - 4 hour
2 - 4 hour
in desiccant air dryer
Injection Pressure 40.0 - 110 MPa
5800 - 16000 psi
Back Pressure 1.00 - 2.00 MPa
145 - 290 psi
Descriptive Properties Value Comments
Holding Pressure () 20-40
% of injection pressure
Injection Speed () High
Scratch Resistance, 10N (dL) 1.8
10N Fine Structure; ISO 1518/D65