Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
Manufacturer | Techmer ES |
Trade Name | Plaslube® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Techmer ES Plaslube® J-1/30/TF/22 NAT PA66.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 |
Water Absorption | 0.60 % | 0.60 % | 24 Hrs; ASTM D570 |
Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Rockwell R | 119 | 119 | ASTM D785 |
Tensile Strength at Break | 159 MPa | 23000 psi | ASTM D638 |
Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
Flexural Strength | 238 MPa | 34500 psi | ASTM D790 |
Flexural Modulus | 9.31 GPa | 1350 ksi | ASTM D790 |
Compressive Strength | 193 MPa | 28000 psi | ASTM D695 |
Izod Impact, Notched | 1.33 J/cm | 2.50 ft-lb/in | ASTM D256 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 43.2 µm/m-°C @Temperature 20.0 °C |
24.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 490 °F | ASTM D648 |
Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |