- Polykemi AB POLYblend 65FS GF10 PC/ABS-blend, Glass Fiber reinforced
Polykemi AB POLYblend 65FS GF10 PC/ABS-blend, Glass Fiber reinforced
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | Polykemi AB |
| Trade Name | POLYblend |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYblend 65FS GF10 PC/ABS-blend, Glass Fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Filler Content | 10 % | 10 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | With Flow; ISO 2577 |
| 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 60.0 MPa | <= 8700 psi | ISO/R527 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO/R527 |
| Flexural Strength | <= 110 MPa | <= 16000 psi | ISO 178 |
| Flexural Modulus | 3.80 GPa @Temperature 23.0 °C |
551 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 115 °C @Load 5.001 kg |
239 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 280 °C | 464 - 536 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Drying Temperature | 100 - 110 °C | 212 - 230 °F | |
| Dry Time | 2 - 8 hour | 2 - 8 hour | in circulation dryer |
| 2 - 8 hour | 2 - 8 hour | in fresh-air dryer | |
| 2 - 8 hour | 2 - 8 hour | in desiccant air dryer | |
| Injection Pressure | 90.0 - 150 MPa | 13100 - 21800 psi | |
| Back Pressure | 0.500 - 1.50 MPa | 72.5 - 218 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Holding Pressure () | 20-50 | % of injection pressure |
| Injection Speed () | High |
Users viewing this material also viewed the following:
- Polymax® Maxelast® F02-087A TPE, Halogen Free Extrusion Grade
- Dow Questra® EA513 High Heat Syndiotactic Polystyrene, 30% Glass Filled (discontinued **)
- Eastman E6838-913P Polyethylene (discontinued **)
- Nitriflex N-5 NBR - Nitrile Rubber
- Mateck Magnesium Fluoride (MgF2)
- Hexcel® HexPly® 916 120°C Curing Epoxy Matrix
- Covestro Baygal® 90 IK 20 Polyurethane
- ATI Allvac® Vasco® 4340 Specialty Steel, Heat Treatment: 899°C (1650°F) Q+T
- BASF N-Ethylpiperazine
Copyright © lookpolymers.com All Rights Reserved