Polykemi AB POLYabs F00 GF15 ABS, Glass Fiber-Reinforced

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 10% Glass Fiber Filled , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled
Manufacturer Polykemi AB
Trade Name POLYabs
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYabs F00 GF15 ABS, Glass Fiber-Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Filler Content 15 %
15 %
±2%; Polykemi
Linear Mold Shrinkage 0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
With Flow; ISO 2577
0.0020 - 0.0040 cm/cm
0.0020 - 0.0040 in/in
Across Flow; ISO 2577
Melt Index of Compound 8.0 g/10 min

@Load 5.00 kg,
Temperature 230 °C
 8.0 g/10 min

@Load 11.0 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 42.0 MPa
<= 6090 psi
ISO/R527
Elongation at Break 4.5 %
4.5 %
ISO/R527
Flexural Strength <= 73.0 MPa
<= 10600 psi
ISO 178
Flexural Modulus 3.70 GPa

@Temperature 23.0 °C
 537 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 0.700 J/cm²

@Temperature 23.0 °C
 3.33 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 105 °C
221 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 95.0 °C
203 °F
120°C/h; ISO 75/1
Vicat Softening Point 103 °C

@Load 5.001 kg
 217 °F

@Load 11.03 lb
 50°C/h; ISO 306
108 °C

@Load 1.00 kg
 226 °F

@Load 2.21 lb
 50°C/h; ISO 306
Processing Properties Metric English Comments
Melt Temperature 190 - 230 °C
374 - 446 °F
Mold Temperature 60.0 - 80.0 °C
140 - 176 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 4 hour
2 - 4 hour
in circulation dryer
2 - 4 hour
2 - 4 hour
in fresh-air dryer
2 - 4 hour
2 - 4 hour
in desiccant air dryer
Injection Pressure 90.0 - 150 MPa
13100 - 21800 psi
Back Pressure 1.00 - 1.50 MPa
145 - 218 psi
Descriptive Properties Value Comments
Holding Pressure () 20-40
% of injection pressure
Injection Speed () High