PolyOne Nymax™ GF 924 33 UV Black 108 Polyamide 66 (Nylon 66)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Nymax™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Nymax™ GF 924 33 UV Black 108 Polyamide 66 (Nylon 66).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Property data for molded test bars: Dry as MoldedInformation provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Density | 1.40 g/cc | 0.0506 lb/in³ | ISO 1183 |
| Water Absorption | 0.90 % | 0.90 % | 24h/23C; ISO 62 |
| 1.0 % | 1.0 % | @ 24 hrs; ASTM D570 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 136 MPa | 19700 psi | ISO 527 |
| Tensile Strength, Yield | 169 MPa | 24500 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 8.8 % | 8.8 % | ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 1.82 GPa | 264 ksi | ISO 527 |
| 8.62 GPa | 1250 ksi | ASTM D638 | |
| 8.78 GPa | 1270 ksi | ISO 178 | |
| Flexural Strength | 172 MPa | 24900 psi | ASTM D790 |
| 207 MPa | 30000 psi | ISO 178 | |
| Flexural Modulus | 8.62 GPa | 1250 ksi | ASTM D790 |
| Izod Impact, Notched | 0.910 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
1.70 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 227 °C | 441 °F | Annealed; ISO 75-2/A |
| 221 °C @Thickness 3.18 mm |
430 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 271 - 293 °C | 520 - 559 °F | |
| Mold Temperature | 82.2 - 107 °C | 180 - 225 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | UV Stabilizer | |
| Appearance | Black | |
| Features | General Purpose | |
| Good UV Resistance | ||
| Heat Stabilized | ||
| Filler / Reinforcement | Glass Fiber Reinforcement, 33% Filler by Weight | |
| Forms | Pellets | |
| Generic Material | Nylon 66 | |
| Generic Name | Polyamide 66 (Nylon 66) | |
| Processing Method | Injection Molding | |
| Regional Availability | North America | |
| South America | ||
| Uses | Automotive Applications | |
| Construction Applications | ||
| Consumer Applications | ||
| General Purpose | ||
| Industrial Applications |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Echo® RPC40G BK Polypropylene Homopolymer
- NOVA Chemicals Novapol® TR-0735-UG Hexene MDPE Rotational Molding Resin
- Saint-Gobain CHR® 2265-2 Extruded PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- Struktol MONTAN WAX OP Lubricant, Processing Additive
- A. Schulman ComAlloy® E-16558 30% Glass Fiber Reinforced Nylon
- Unitika TERRAMAC TE-7000 Polylactic Acid (PLA)
- EPICHEM Epilon G2-PC 10% GF Polycarbonate, 10% Glass Fiber
- 3M Pronto™ CA-9 Instant Adhesive
- Braskem CP 145 Injection Molding Polypropylene
Copyright © lookpolymers.com All Rights Reserved