LATI Latamid 66 MDT03-01 PA 66

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	LATI
Trade Name	Latamid
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latamid 66 MDT03-01 PA 66.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polyamide 66 (PA66) based compound. Magnetic detectable filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	1.28 g/cc	0.0462 lb/inÂ³
Linear Mold Shrinkage, Flow	0.0060 - 0.010 cm/cm	0.0060 - 0.010 in/in
Linear Mold Shrinkage, Transverse	0.0060 - 0.010 cm/cm	0.0060 - 0.010 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	60.0 MPa @Temperature 23.0 Â°C	8700 psi @Temperature 73.4 Â°F
Elongation at Break	18 % @Temperature 23.0 Â°C	18 % @Temperature 73.4 Â°F
Elongation at Yield	12 %	12 %
Tensile Modulus	2.85 GPa @Temperature 23.0 Â°C	413 ksi @Temperature 73.4 Â°F
Charpy Impact Unnotched	10.0 J/cmÂ²	47.6 ft-lb/inÂ²
Charpy Impact, Notched	0.500 J/cmÂ²	2.38 ft-lb/inÂ²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	250 Â°C	482 Â°F
Deflection Temperature at 1.8 MPa (264 psi)	230 Â°C	446 Â°F
Vicat Softening Point	250 Â°C @Load 5.00 kg	482 Â°F @Load 11.0 lb

Processing Properties	Metric	English
Melt Temperature	270 - 290 Â°C	518 - 554 Â°F
Mold Temperature	80.0 - 100 Â°C	176 - 212 Â°F
Drying Temperature	90.0 - 100 Â°C @Time 10800 sec	194 - 212 Â°F @Time 3.00 hour

Descriptive Properties	Value	Comments
ISO Shrinkage - Pressure	60 MPa