Eurostar Staramide RF008U PA66/6, 40% Glass Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 40% Glass Fiber Reinforced |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide RF008U PA66/6, 40% Glass Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide RF008U is a 40% Glass Fiber Reinforced Polyamide 66/Polyamide 6 Injection Molding Resin (also known as Staramide 66 C 40V S4)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 4.00 mm |
0.0020 - 0.0040 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 189 MPa | 27400 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| Flexural Strength | 276 MPa | 40000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | 80x10x4; ISO 179/1eA |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
15.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 258 °C | 496 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 260 - 280 °C | 500 - 536 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 290 °C | 518 - 554 °F | |
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- MV Labs CD410 CdCl2·xH2O Cadmium chloride hydrate
- SABIC Innovative Plastics Lexan® FL2000 PC
- LATI Later 4 G/20 PBT, 20% Glass Fiber Reinforced
- Teknor Apex Sinvicomp SBB 3704 Polyvinyl Chloride, Rigid
- A. Schulman SCHULAMID® 6 GF50H 50% Glass Fiber Reinforced Nylon 6
- BASF Neopolen® P 8225 K 0.05 g/cc Core density; Expanded Polypropylene (Europe)
- Wanhua Chemical Wanthane® WHT-6233 TPU Hot-Melt Adhesive
- BASF Neopolen® P 9270 0.11 g/cc Core density; Expanded Polypropylene (Europe)
Copyright © lookpolymers.com All Rights Reserved