- PolyOne Lubri-Tech™ AT-15MCF/15T Acetal-Copolymer, Carbon Fiber Reinforced, PTFE Lubricated (discontinued **)
PolyOne Lubri-Tech™ AT-15MCF/15T Acetal-Copolymer, Carbon Fiber Reinforced, PTFE Lubricated (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ AT-15MCF/15T Acetal-Copolymer, Carbon Fiber Reinforced, PTFE Lubricated
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Milled Carbon Fiber ReinforcedPTFE LubricatedUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 58.6 MPa | 8500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 4.48 GPa | 650 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Izod Impact, Notched | 0.400 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
0.750 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+6 - 1.00e+13 ohm-cm | 1.00e+6 - 1.00e+13 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 188 - 210 °C | 370 - 410 °F | Molding |
| Mold Temperature | 48.9 - 93.3 °C | 120 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Renegade Materials Corporation RM-3000 Bismaleimide (BMI) 6781 S2 Glass Fabric
- Mallard Creek Polymers ROVENE® 6020 SBR Latex
- Karina 40/418-FC-LMP Green Color Concentrate for PVC
- Sylvin Technologies 916V0 Black PVC for Injection Molding
- Schott D 263® T eco Thin Borosilicate Optical Glass
- A. Schulman POLYTROPE™ TPP 512 Injection Molding Grade Olefinic Thermoplastic Elastomer
- Unipetrol C9 Fraction Redistillated
- Axiall LSS-8200 Rigid PVC, Extrusion
- Addiplast Addinyl C2 ZV15 Nylon 66/6, 15% Glass Filled
Copyright © lookpolymers.com All Rights Reserved