SABIC Innovative Plastics LNP STAT-KON RE007 PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON RE007 PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* RE007 is a compound based on PA66 resin containing 35% Carbon Fiber. Added features include: Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.33 g/cc | 1.33 g/cc | ASTM D792 |
| Density | 1.322 g/cc | 0.04776 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.590 % | 0.590 % | 50% RH, 24 hrs; ASTM D570 |
| 0.920 % | 0.920 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.011 cm/cm @Time 86400 sec |
0.0090 - 0.011 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 275 MPa | 39900 psi | Type I, 5 mm/min; ASTM D638 |
| 282 MPa | 40900 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 |
| 1.7 % | 1.7 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 29.92 GPa | 4340 ksi | 5 mm/min; ASTM D638 |
| 30.41 GPa | 4411 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 387 MPa | 56100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 391 MPa | 56700 psi | ISO 178 | |
| Flexural Modulus | 24.3 GPa | 3520 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 24.61 GPa | 3569 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.03 J/cm | 1.93 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.3 J/cm | 19.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 62.0 kJ/m² | 29.5 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 24.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
13.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 37.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
20.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 262 °C | 504 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 263 °C @Thickness 3.20 mm |
505 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 256 °C | 493 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 257 °C @Thickness 3.20 mm |
495 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 100 ohm - 1e+05 | 100 ohm - 1e+05 | ASTM D257 |
Users viewing this material also viewed the following:
- Rogers Corporation Poron® Shock Seal™ 4790-79-20 Urethane Foam, Industrial Grade
- PolyOne Geon™ Vinyl Flexible B6D00 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Industrial Laminates/Norplex NP322 Cotton Fabric
- Techmer ES Electrablend® POM C BK Acetal
- Samsung Cheil Industries Starex® ES-0173 ABS, Extrusion Grade
- CLAL-MSX NICLAFOR® 1000 TD4 Quenched/Cold Rolled, Rolled Copper Alloy
- Alliance Polymers Zythane™ 7085AF Thermoplastic Polyurethane Elastomer
- ConocoPhillips 22 Super Hydraulic Oil
Copyright © lookpolymers.com All Rights Reserved